Method for draping composite materials on a form and material suitable for said method
The subject matter of the invention is a method for draping on a form, which includes a step of deposition on the form of a first fold support in the form of one or more polymer nonwoven fabrics. The invention further relates to a thermoplastic nonwoven material manufactured with a nonwoven fabric of polymer fibers.
1. A process of drape forming parts made of thermoplastic composite materials on a former, the process comprising:
laying up on the former a support ply in the form of one or more polymer nonwoven fabrics;
melting said support ply at a lower or equal temperature than the thermoplastic composite material of said part to provide a coupling surface for a first ply of a thermoplastic composite material part to be drape formed on the former;
draping said first ply on said support ply;
draping further plies of said part; and
heating of the thermoplastic composite material part on said former and melting further at least part of said support ply of said polymer nonwoven fabric for promoting adhesion of the first ply of said part to the former.
2. The drape-forming process as claimed in claim 1 , further comprising a step of needlepunching the one or more polymer nonwoven fabrics prior to the lay-up.
3. The drape-forming process as claimed in claim 2 , wherein the needlepunching step is a needlepunching of 50 to 130 strokes/minute.
4. The drape-forming process as claimed in claim 1 further comprising a step of hydroentangling the one or more polymer nonwoven fabrics prior to the lay-up.
5. The drape-forming process as claimed in claim 4 , wherein the prior hydroentangling step is carried out at a pressure of the order of 40 to 80 bar.
6. The drape-forming process as claimed in claim 1 , further comprising a step of calendering the one or more polymer nonwoven fabrics prior to the lay-up.
7. The drape-forming process as claimed in claim 1 , further comprising needlepunching, hydroentangling and calendering steps prior to the lay-up, the order of the steps being needlepunching then hydroentangling then calendering.
8. The drape-forming process as claimed in claim 1 , wherein the one or more polymer nonwoven fabrics comprise polymer fibers of a first nature.
9. The drape-forming process as claimed in claim 1 , wherein the one or more polymer nonwoven fabrics comprise polymer fibers of two different natures.
10. The drape-forming process as claimed in claim 1 , further comprising a step of clamping the one or more polymer nonwoven fabrics to the former.
11. The drape-forming process as claimed in claim 10 , wherein the step of clamping comprises a clamping selected from a mechanical clamping using screwed or clamped blocks, an electromagnetic clamping with the aid of a magnet, clamping by means of adhesive tapes or clamping by coupling strips.
12. The drape-forming process as claimed in claim 1 , further comprising a step of melting the material of the one or more polymer nonwoven fabrics.
13. The drape-forming process as claimed in claim 1 , further comprising a step of introducing resin by partial melting of the polymer fibers of the one or more polymer nonwoven fabrics.