Sulfide solid electrolyte material, battery, and producing method for sulfide solid electrolyte material
The main object of the present invention is to provide a sulfide solid electrolyte material having favorable ion conductivity and high stability against moisture. The present invention solves the above-mentioned problem by providing a sulfide solid electrolyte material comprising an M 1 element (such as Li element), an M 2 element (such as Ge element, Sn element and P element) and a S element, and having a peak at a position of 2θ=29.58°±0.50° in X-ray diffraction measurement using a CuKα ray, characterized in that when a diffraction intensity at the above-mentioned peak of 2θ=29.58°±0.50° is regarded as IA and a diffraction intensity at a peak of 2θ=27.33°±0.50° is regarded as IB, a value of IB/IA is less than 0.50, and the M 2 contains at least P and Sn.
1. A sulfide solid electrolyte material comprising:
a composition of Li (4−x) (M 2 ′ (1−δ) Sn δ ) (1−x) P x S 4 , where
M 2 ′ represents the element selected from the group consisting of Si, Ge, Ti, Zr, Nb and combinations thereof,
0<δ≤1, and
0<x<1,
wherein
the sulfide solid electrolyte material has a peak at a position of 2θ=29.58°±0.50° in X-ray diffraction measurement using a CuKα ray;
the sulfide solid electrolyte material satisfies conditions (i) or (ii):
(i) the sulfide solid electrolyte material does not have a peak at a position of 2θ=27.33°±0.50° in X-ray diffraction measurement using a CuKα ray, or
(ii) when a diffraction intensity at the peak of 2θ=29.58°±0.50° is regarded as I A and a diffraction intensity at a peak of 2θ=27.33°±0.50° is regarded as I B , a value of I B I A is less than 0.50 but not 0.
2. The sulfide solid electrolyte material according to claim 1 , wherein condition (ii) is satisfied.
3. The sulfide solid electrolyte material according to claim 1 , wherein 0<δ<1.
4. The sulfide solid electrolyte material according to claim 1 , wherein 0.2≤δ≤1.
5. The sulfide solid electrolyte material according to claim 1 , wherein the sulfide solid electrolyte material has a composition of Li (4−x) Sn (1−x) P x S 4 , where:
0.65≤x≤0.75.
6. The sulfide solid electrolyte material according to claim 1 , wherein an a-axial length of a lattice constant is 8.70 Å or more in a crystal phase having the peak at the position of 2θ=29.58°±0.50°.
7. A sulfide solid electrolyte material comprising a crystal structure as a main body, the crystal structure includes:
an octahedron O composed of Li and S;
a tetrahedron T 1 composed of an M 2 ′ element, and, the tetrahedron T 1 and the octahedron O sharing an edge; and
a tetrahedron T 2 composed of an M 2 ′ element and, the tetrahedron T 2 and the octahedron O sharing a corner;
P is present in at least one of tetrahedron T 1 and tetrahedron T 2 , and
Sn is present in at least one of tetrahedron T 1 and tetrahedron T 2 ;
wherein
the sulfide solid electrolyte material has a composition of Li (4−x) (M 2 ′ (1−δ) Sn δ ) (1−x) P x S 4 , where
M 2 ′ represents the element selected from the group consisting of Si, Ge, Ti, Zr, Nb and combinations thereof, and may be the same or different in tetrahedron T 1 and tetrahedron T 2 ,
0<δ≤1, and
0<x<1.
8. The sulfide solid electrolyte material according to claim 7 , wherein 0<δ<1.
9. The sulfide solid electrolyte material according to claim 7 , wherein 0.2≤δ≤1.
10. The sulfide solid electrolyte material according to claim 7 , wherein an a-axial length of a lattice constant is 8.70 Å or more in the crystal structure.
11. A battery comprising
a cathode active material layer containing a cathode active material,
an anode active material layer containing an anode active material, and
an electrolyte layer formed between the cathode active material layer and the anode active material layer,
wherein at least one of the cathode active material layer, the anode active material layer and the electrolyte layer contains the sulfide solid electrolyte material according to claim 1 .
12. A battery comprising
a cathode active material layer containing a cathode active material,
an anode active material layer containing an anode active material, and
an electrolyte layer formed between the cathode active material layer and the anode active material layer,
wherein at least one of the cathode active material layer, the anode active material layer and the electrolyte layer contains the sulfide solid electrolyte material according to claim 7 .
13. A method for producing the sulfide solid electrolyte material according to claim 1 , the method comprising:
synthesizing an amorphized ion conductive material by mechanical milling while using a raw material composition containing the M 1 element, the M 2 element, and the S element, and
obtaining the sulfide solid electrolyte material by heating the amorphized ion conductive material.
14. A method for producing the sulfide solid electrolyte material according to claim 7 , the method comprising:
synthesizing an amorphized ion conductive material by mechanical milling while using a raw material composition containing the M 1 element, the M 2a element, the M 2b element, and the S element, and
obtaining the sulfide solid electrolyte material by heating the amorphized ion conductive material.
15. The sulfide solid electrolyte material according to claim 1 , wherein condition (i) is satisfied.
16. The sulfide solid electrolyte material according to claim 1 , wherein a molar fraction of the Li element is 3.35 or less based on a total molar fraction of P and the M 2 ′ element of 1.
17. The sulfide solid electrolyte material according to claim 1 , wherein
0.65≤x≤0.75.