Ferritic stainless steel sheet
To provide a ferritic stainless steel sheet which has high scale spalling even at a high temperature around 1000° C. Provided is a ferritic stainless steel sheet having excellent Mn-containing oxide film-forming ability and scale spalling ability, containing, in terms of mass %: C: 0.001 to 0.020%, N: 0.001 to 0.020%, Si: 0.10 to 0.40%, Mn: 0.20 to 1.00%, Cr: 16.0 to 20.0%, Nb: 0.30 to 0.80%, Mo: 1.80 to 2.40%, W: 0.05 to 1.40%, Cu: 1.00 to 2.50%, and B: 0.0003 to 0.0030%, in which the above-mentioned components are contained satisfying the formula (1) below, and the balance is composed of Fe and inevitable impurities. At least one of N, Al, V, Mg, Sn, Co, Zr, Hf, and Ta may be added in a predetermined content range. 3≦(5×Mo)/(3×Mn)≦20 (1)
1. A Mn-containing ferritic stainless steel sheet consisting of, in terms of mass %:
C: 0.001 to 0.020%,
N: 0.001 to 0.020%,
Si: 0.10 to 0.40%,
Mn: 0.20 to 1.00%,
Cr: 16.0 to 20.0%,
Nb: 0.30 to 0.80%,
Mo: 1.80 to 2.40%,
W: 0.05 to 1.40%,
Cu: 1.00 to 2.50%, and
B: 0.0003 to 0.0030%, satisfying formula (1) below,
and a balance is composed of Fe and inevitable impurities,
5≦(5×Mo)/(3×Mn)≦20 (1),
wherein Mo and Mn in the formula (1) each mean the content (mass %) thereof.
2. The Mn-containing ferritic stainless steel sheet according to claim 1 , satisfying formula (2) below,
2.28≦(5×Mo+2.5×W)/(4×Mn)≦8.0 (2),
wherein Mo, Mn, and W in the formula (2) each mean the content (mass %) thereof.
3. The Mn-containing ferritic stainless steel sheet according to claim 2 , wherein (Mn, Cr) 3 O 4 is generated on an outermost layer of an oxide film when a heat treatment is performed in a condition of 900 to 1000° C.×100 hours or longer.
4. The Mn-containing ferritic stainless steel sheet according to claim 2 , wherein an amount of spalled scale in cases in which the ferritic stainless steel sheet is subjected to a continuous oxidation test in air at 1000° C. for 200 hours is 1.0 mg/cm 2 or smaller.
5. The Mn-containing ferritic stainless steel sheet according to claim 1 , wherein (Mn, Cr) 3 O 4 is generated on an outermost layer of an oxide film when a heat treatment is performed in a condition of 900 to 1000° C.×100 hours or longer.
6. The Mn-containing ferritic stainless steel sheet according to claim 5 , wherein an amount of spalled scale in cases in which the ferritic stainless steel sheet is subjected to a continuous oxidation test in air at 1000° C. for 200 hours is 1.0 mg/cm 2 or smaller.
7. The Mn-containing ferritic stainless steel sheet according to claim 1 , wherein an amount of spalled scale in cases in which the ferritic stainless steel sheet is subjected to a continuous oxidation test in air at 1000° C. for 200 hours is 1.0 mg/cm 2 or smaller.