Processes for treating fly ashes
There are provided processes for treating fly ash. For example, the processes can comprise leaching fly ash with HCl so as to obtain a leachate comprising aluminum ions and a solid, and separating the solid from the leachate; reacting the leachate with HCl so as to obtain a liquid and a precipitate comprising the aluminum ions in the form of AlCl 3 , and separating the precipitate from the liquid; and heating the precipitate under conditions effective for converting AlCl 3 into Al 2 O 3 and optionally recovering gaseous HCl so-produced.
1. A process for treating raw fly ash, said process comprising:
optionally a pre-leaching treatment that consists of reducing the particle size of said raw fly ash;
leaching said raw fly ash with HCl so as to obtain a leachate comprising aluminum ions and iron ions and a solid, and separating said solid from said leachate;
reacting said leachate with HCl so as to obtain a liquid comprising iron ions and a precipitate comprising said aluminum ions in the form of AlCl 3 , and separating said precipitate from said liquid; and
heating said precipitate under conditions effective for converting AlCl 3 into Al 2 O 3 and optionally recovering gaseous HCl so-produced.
2. The process of claim 1 , wherein said fly ash is leached with HCl having a concentration of about 25 to about 45 weight %.
3. The process of claim 2 , wherein said process further comprises recycling said gaseous HCl so-produced by contacting it with water so as to obtain a composition having a concentration of about 25 to about 45 weight % and using said composition for leaching said fly ash.
4. The process of claim 1 , wherein said fly ash is leached with HCl having a concentration of about 25 to about 45 weight % at a temperature of about 125 to about 225° C.
5. The process of claim 4 , wherein said fly ash is leached at a pressure of about 4 to about 10 barg (about 400 KPag to about 1000 KPag).
6. The process of claim 5 , wherein said process is effective for avoiding producing red mud.
7. The process of claim 1 , wherein said fly ash is leached with HCl having a concentration of about 25 to about 45 weight % at a temperature of about 160 to about 190° C.
8. The process of claim 1 , wherein said fly ash is leached with HCl having a concentration of about 18 to about 45 weight %.
9. The process of claim 1 , wherein said fly ash is leached with HCl having a concentration of about 18 to about 45 weight % at a temperature of about 125 to about 225° C.
10. The process of claim 1 , wherein said recycled gaseous HCl so-produced is contacted with water so as to obtain said composition having a concentration between 18 and 36 weight %.
11. The process of claim 1 , wherein said process comprises reacting said leachate with gaseous HCl so as to obtain said liquid and said precipitate comprising said aluminum ions, said precipitate being formed by crystallization of AlCl 3 ·6H 2 O.
12. The process of claim 11 , wherein during said crystallization of AlCl 3 ·6H 2 O, said liquid is maintained at a concentration of HCl of about 25 to about 35% by weight.
13. The process of claim 12 , wherein said crystallization is carried out at a temperature of about 45 to about 65° C.
14. The process of claim 11 , wherein said process comprises heating said precipitate at a temperature of about 350° C. to about 500° C. for converting AlCl 3 ·6H 2 O into Al 2 O 3 .
15. The process of claim 1 , wherein said process comprises reacting said leachate with HCl recovered during said processs and having a concentration of at least 30% by weight as to obtain said liquid and said precipitate comprising said aluminum ions, said precipitate being formed by crystallization of AlCl 3 .6H 2 O.
16. The process of claim 15 , wherein said crystallization is carried out at a temperature of about 45 to about 65° C.
17. The process of process of claim 1 , wherein said process comprises converting AlCl 3 ·6H 2 O into Al 2 O 3 by carrying out a calcination of AlCl 3 .6H 2 O, said calcination comprising steam injection.
18. The process of process of claim 17 , wherein said steam is overheated.
19. The process of claim 1 , wherein said fly ash is leached at a pressure of about 4 to about 10 barg (about 400 KPag to about 1000 KPag).
20. A process for preparing aluminum, said process comprising :
optionally a pre-leaching treatment that consists of reducing the particle size of raw fly ash;
leaching said raw fly ash with HCl so as to obtain a leachate comprising aluminum ions and iron ions and a solid, and separating said solid from said leachate;
reacting said leachate with HCl so as to obtain a liquid comprising iron ions and a precipitate comprising said aluminum ions in the form of AlCl 3 , and separating said precipitate from said liquid;
heating said precipitate under conditions effective for converting AlCl 3 into Al 2 O 3 and optionally recovering gaseous HCl so-produced; and
converting said Al 2 O 3 into aluminum.