Sintered member, pinion gear for starters, and production method therefor
View Patent ↗The present invention provides a sintered body and a production method therefor in which effects of pores remaining at a surface of the sintered body can be avoided without removing the pores by machining and plastic working, thereby obtaining strength equivalent to that of ingot materials. The sintered member comprises: a hardness distribution in which hardness contiguously varies from a surface to an inner portion; a Vickers hardness value of 730 or less at the surface; the maximum hardness of which portion exists in a region of 150 to 300 μm from the surface; wherein the maximum hardness is a Vickers hardness value of 600 or more.
1. A sintered member comprising:
a hardness distribution in which hardness continuously varies from a surface to an inner portion;
a Vickers hardness value of 730 or less at the surface;
the maximum hardness of which portion exists in a region of 150 to 300 μm from the surface;
wherein the maximum hardness is Vickers hardness value of 600 or more,
a carburized and hardened layer is formed in a surface layer, and a decarburized layer that has a lower carbon concentration than that of the carburized and hardened layer is formed outside the carburized and hardened layer, and the decarburized layer forms the surface.
2. The sintered member according to claim 1 , wherein the carburized and hardened layer has a carbon concentration of 0.7 to 1.2 mass % and the decarburized layer has a carbon concentration of 0.3 to 0.6 mass %.
3. A pinion gear made of the sintered member according to claim 1 .
4. A production method for a sintered member of claim 1 , the method comprising:
a mixing step for mixing a raw material powder;
a compacting step for compressing the raw material powder and obtaining a compact;
a sintering step for sintering the compact and obtaining a sintered body;
a forging step for forging the sintered body and obtaining a forged body;
a carburizing step for heating the forged body in a gas atmosphere in which the carbon concentration is 0.7 to 1.2 mass % at a temperature of 850 to 950° C.;
a decarburizing step for heating the forged body in a carburizing gas atmosphere in which the carbon concentration is 0.3 to 0.6 mass % at a temperature of 800 to 950° C. after the carburizing step;
a quenching step for rapidly cooling the forged body after the decarburizing step; and
a tempering step for heating the forged body to a temperature of 150 to 280° C. and cooling the forged body to ordinary temperature after the quenching step.
5. The production method for a sintered member according to claim 4 , wherein the decarburizing step is performed sequentially after the carburizing step while heating the forged body and displacing the atmosphere gas.
6. The production method for a sintered member according to claim 4 , wherein the quenching is performed by dipping the forged body into an oil immediately after the carburizing step, and the decarburizing step is performed by again heating the forged body.
7. The production method for a sintered member according to claim 4 , wherein the forged body has a density ratio of 97.8% or more after the forging step.
8. The production method for a pinion gear for starter produced by the production method for a sintered member according to claim 4 .
9. The sintered member according to claim 2 , wherein the carbon concentration is maximum at an intermediate portion of the carburized and hardened layer in a depth direction thereof, gradually reduces from the maximum carbon concentration portion toward the decarburized layer, and gradually reduces from the decarburized layer toward the surface.