Separator
Provided is a separator which shows excellent performance in electric insulation, electrolyte-holding property and ion- or electron-permeability and which can be stably manufactured. The separator is configured from a laminate non-woven fabric consisting of at least two layers, said layers including a non-woven fabric layer (layer I) that comprises a synthetic fiber having a fiber size of 0.1 μm or greater and less than 4.0 μm and a non-woven fabric layer (layer II) that comprises a thermoplastic resin fiber having a fiber size of 4.0-30.0 μm inclusive, and has a weight per area of 3.0 g/m 2 or greater and less than 20.0 g/m 2 .
1. A separator composed of at least two layers of laminated nonwoven fabric comprising:
a nonwoven fabric layer (layer I), composed of synthetic fibers having a fiber diameter of 0.1 μm to less than 4.0 μm, and
a nonwoven fabric layer (layer II), composed of a thermoplastic resin fibers having a fiber diameter of 4.0 μm to 30 μm;
wherein, the basis weight thereof is 3.0 g/m 2 to less than 20.0 g/m 2 ,
wherein the laminated nonwoven fabric is composed nonwoven fabric, laminate in which the coefficient of variation of the texture of the nonwoven fabric is less than 1.7, and
wherein the separator is set in an electrochemical cell or an electrical energy storage device in which an electrolytic solution is injected.
2. The separator according to claim 1 , wherein the layer I is present as an intermediate layer between two of the layers II.
3. The separator according to claim 1 , wherein the layer II is present as an intermediate layer between two of the layers I.
4. The separator according to any one of claims 1 to 3 , wherein the thermoplastic resin fibers in the nonwoven fabric layer (layer II) are thermoplastic synthetic continuous long fibers.
5. The separator according to claim 1 , wherein the laminated nonwoven fabric is formed by integrating by chemical and/or thermal bonding.
6. The separator according to claim 1 , wherein the laminated nonwoven fabric has a thickness of 10 μm to 50 μm.
7. The separator according to claim 1 , wherein the nonwoven fabric layer (layer I) is formed by melt-blowing.
8. The separator according to claim 4 , wherein the ratio (i)/(ii) of the basis weight (i) of the nonwoven fabric layer (layer I) to the basis weight (ii) of the nonwoven fabric layer (layer II) in the laminated nonwoven fabric is 1/10 to 10/1.
9. The separator according to claim 1 , wherein the laminated nonwoven fabric is calendered.
10. The separator according to claim 1 , wherein the laminated nonwoven fabric is hydrophilized.
11. The separator according to claim 1 , wherein an inorganic material is compounded in the laminated nonwoven fabric.
12. An electrochemical cell or energy storage device that uses the separator according to claim 1 .