Adhesive tape substrate, adhesive tape, and methods for producing same
An adhesive tape substrate production method disclosed in the present description includes the steps of: decreasing the amount of a sizing agent contained in a glass cloth by heat; impregnating the glass cloth for which the amount of the sizing agent has been decreased with a dispersion of a fluorine resin; and heating the impregnated glass cloth to a temperature equal to or higher than a melting point of the fluorine resin. Thus, an adhesive tape substrate including the glass cloth impregnated with the fluorine resin is obtained. This method are more productive of adhesive tape substrates and adhesive tapes than conventional methods. In addition, adhesive tape substrates and adhesive tapes for which the occurrence of defects in appearance are reduced can be produced.
1. A method for producing an adhesive tape substrate, comprising:
(i) decreasing an amount of a sizing agent contained in a glass cloth by first heating;
(ii) impregnating a first time the glass cloth, in which the amount of the sizing agent has been decreased by the first heating, with a dispersion of a fluorine resin; and
(iii) heating the impregnated glass cloth to a temperature equal to or higher than a melting point of the fluorine resin by second heating so as to obtain an adhesive tape substrate comprising the glass cloth impregnated with the fluorine resin.
2. The method for producing an adhesive tape substrate according to claim 1 ,
wherein the amount of the sizing agent contained in the glass cloth is decreased to an amount in a range from 0.5 to 3 weight % of the glass cloth.
3. The method for producing an adhesive tape substrate according to claim 1 ,
wherein the fluorine resin is polytetrafluoroethylene.
4. A method for producing an adhesive tape, further comprising: providing an adhesive agent layer on one surface of an adhesive tape substrate obtained by the method according to claim 1 .
5. The method for producing an adhesive tape substrate according to claim 1 ,
wherein the first heating is performed at a temperature in a range of 300° C. or higher and 340° C. or lower.
6. The method for producing an adhesive tape substrate according to claim 1 ,
wherein the adhesive tape substrate comprises the impregnated glass cloth comprising glass yarns that have a cross-section having an aspect ratio in a range of 0.15 or larger.