Rigid IPVC pipe resin composition exhibiting excellent strength and hydrostatic pressure resistance and rigid IPVC pipe
View Patent ↗Provided are: a rigid IPVC pipe resin composition, which exhibits excellent strength and hydrostatic pressure resistance, including a PVC resin having a K-value from 72 to 84; and a rigid IPVC pipe, which exhibits excellent strength and hydrostatic pressure resistance, manufactured by extrusion of the resin composition.
1. A rigid IPVC pipe resin composition, which exhibits excellent strength and hydrostatic pressure resistance, comprising:
a PVC resin having a K-value from 72 to 84; and
1 part by weight to 10 parts by weight of a methacrylate lubricant, based on 100 parts by weight of the PVC resin, wherein the methacrylate lubricant comprises a mixture of butyl methacrylate monomer represented by Formula (I) and methyl methacrylate monomer represented by Formula (II) in a weight ratio of 1:1 to 1:2,
wherein the rigid IPVC pipe resin composition is free of a plasticizer,
2. The resin composition according to claim 1 , further comprising:
1 part by weight to 3 parts by weight of a tin stabilizer (tin complex);
3 parts by weight to 10 parts by weight of an impact modifier, based on 100 parts by weight of the PVC resin.
3. A rigid IPVC pipe, which exhibits excellent strength and hydrostatic pressure resistance, comprising:
a PVC resin having a K-value ranging from 72 to 84, and
1 part by weight to 10 parts by weight of a methacrylate based compound, based on 100 parts by weight of the PVC resin, wherein the methacrylate based compound comprises butyl methacrylate monomer represented by Formula (I) and methyl methacrylate monomer represented by Formula (II) in a weight ratio of 1:1 to 1:2,
wherein the rigid IPVC pipe is free of a plasticizer, and
wherein the rigid IPVC pipe has a tensile strength ranging from 50 MPa to 60 MPa,
4. The resin composition according to claim 2 , wherein the tin stabilizer comprises at least one selected from the group consisting of tin mercaptoacetate compounds and tin disulfide.
5. The resin composition according to claim 2 , wherein the impact modifier comprises at least one selected from the group consisting of acrylic copolymers and chloride polyethylene.
6. The rigid IPVC pipe according to claim 3 , further comprising:
1 part by weight to 3 parts by weight of a tin complex; and
3 parts by weight to 10 parts by weight of an impact modifier, based on 100 parts by weight of the PVC resin, wherein the impact modifier comprises chloride polyethylene.
7. The rigid IPVC pipe according to claim 6 , wherein the tin complex comprises at least one selected from the group consisting of tin mercaptoacetate compounds and tin disulfide.