Processes and catalysts for converting alkanes to alkenes
Generally, regenerable, encapsulated metal oxide catalysts comprising a ceramic matrix and metal catalysts may be used to convert alkanes to alkenes. The encapsulated metal oxide catalyst may be tailored to produce a variety of alkenes including ethylene, butylene, and propylene. Further, the encapsulated metal oxide catalysts advantageously allow for regeneration and reactant recovery for cost effective and environmentally friendly processes.
1. A method comprising:
producing a dough comprising a clay, a metal organic salt, and water, wherein the metal organic salt is present in an amount of about 5% to about 50% of a metal of the metal organic salt by weight of the clay;
forming a plurality of pellets from the dough;
drying the pellets;
calcining the pellets so as to form a plurality of encapsulated metal oxide catalysts that comprise a porous ceramic matrix and metal catalysts dispersed therein; and
washing the encapsulated metal oxide catalysts with a water-miscible organic solvent, wherein the encapsulated metal oxide catalysts comprise a plurality of pores containing the metal catalysts having an average diameter of about 5 nm to about 300 nm.
2. The method of claim 1 , wherein the clay comprises at least one selected from the group consisting of a pozzalonic material, kaolin, metakaolin, bentonite, bauxite, illite, vermiculite, Fuller's earth, hectorite, saponite, speiolite, shale, halloysite, pumice, pumicite, montmonillonite, a chlorite clay, a phylosilicate, mica, and any combination thereof.
3. The method of claim 1 , wherein the metal organic salt comprises a salt of (1) a C 1 -C 16 comprising at least one carboxylate and (2) any alkali, basic, or transition metal.
4. The method of claim 3 , wherein the transition metal is magnesium or zinc.
5. The method of claim 1 , wherein the dough further comprise at least one selected from the group consisting of an activation agent, a pore molding agent, and any combination thereof.
6. The method of claim 5 , wherein the pore molding agent comprises at least one selected from the group consisting of glycol, diethylene glycol, glycerin, oligomers of ethylene glycol, malonic acid, succinic acid, and the like, or any combination thereof.
7. The method of claim 5 , wherein the pore molding agent is present in an amount of about 1% to about 50% by weight of the clay.
8. The method of claim 1 , wherein calcining involves heating to a temperature of about 600° C. to about 1000° C. in an oxygen-containing gas stream.
9. The method of claim 1 , wherein the water-miscible organic solvent comprises at least one selected from the group consisting of acetone, an alcohol, and any combination thereof.
10. The of claim 1 , wherein the encapsulated metal oxide catalysts comprise a plurality of pores between clay platelets having an average diameter of about 2 nm to about 50 nm.
11. The method of claim 1 , wherein the encapsulated metal oxide catalysts have a void volume of about 25% to about 85%.
12. The method of claim 1 , wherein the encapsulated metal oxide catalysts have a crush strength of about 10,000 psi or greater.
13. The method of claim 1 , wherein the encapsulated metal oxide catalysts have a crush strength of about 60,000 psi or greater.
14. The method of claim 1 , wherein the clay comprises bentonite and the metal organic salt comprises magnesium carbonate tri-hydrate.
15. The method of claim 1 , wherein the clay comprises bentonite, wherein the metal organic salt comprises magnesium carbonate, and wherein the water-miscible organic solvent comprises methanol.
16. The method of claim 1 , wherein the clay comprises kaolin and the metal organic salt comprises magnesium carbonate tri-hydrate, and wherein the dough further comprises an activation agent that comprises an X-type zeolite.
17. A method comprising:
producing a dough comprising a clay, a metal organic salt, and water, wherein the metal organic salt is present in an amount of about 5% to about 50% of a metal of the metal organic salt by weight of the clay;
forming a plurality of pellets from the dough;
drying the pellets;
calcining the pellets so as to form a plurality of encapsulated metal oxide catalysts that comprise a porous ceramic matrix and metal catalysts dispersed therein; and
washing the encapsulated metal oxide catalysts with a water-miscible organic solvent, wherein the encapsulated metal oxide catalysts have a void volume of about 25% to about 85%.
18. The method of claim 17 , wherein the dough further comprise at least one selected from the group consisting of an activation agent, a pore molding agent, and any combination thereof.
19. The method of claim 18 , wherein the pore molding agent comprises at least one selected from the group consisting of glycol, diethylene glycol, glycerin, oligomers of ethylene glycol, malonic acid, succinic acid, and the like, or any combination thereof.
20. The method of claim 18 , wherein the pore molding agent is present in an amount of about 1% to about 50% by weight of the clay.
21. A method comprising:
producing a dough comprising a clay, a metal organic salt, and water, wherein the metal organic salt is present in an amount of about 5% to about 50% of a metal of the metal organic salt by weight of the clay;
forming a plurality of pellets from the dough;
drying the pellets;
calcining the pellets so as to form a plurality of encapsulated metal oxide catalysts that comprise a porous ceramic matrix and metal catalysts dispersed therein; and
washing the encapsulated metal oxide catalysts with a water-miscible organic solvent, wherein the encapsulated metal oxide catalysts have a crush strength of about 10,000 psi or greater.