Porous cellulose body and method for producing same
A porous body that contains cellulose nanofibers having very thin fiber diameters and high hydrophilicity, and has a large specific surface area, and to provide a method of producing the porous body simply with low cost. A method of producing a porous cellulose comprises a process of lyophilizing a mixed liquid containing cellulose nanofibers and a dispersion medium, wherein the dispersion medium is a mixed dispersion medium of water and an organic solvent dissolving in water, a concentration of the organic solvent in the mixed dispersion medium is 2 to 40 mass %, and a solid content concentration of the cellulose nanofibers in the mixed liquid is 0.001 to 5 mass %.
1. A method of producing a porous cellulose body, the method comprising a process of lyophilizing a mixed liquid containing cellulose nanofibers and a dispersion medium, wherein
the dispersion medium is a mixed dispersion medium of water and an organic solvent dissolving in water,
the concentration of the organic solvent in the mixed dispersion medium is 2 to 40 mass %, and
the solid content concentration of the cellulose nanofibers in the mixed liquid is 0.001 to 5 mass %.
2. The method of producing a porous cellulose body according to claim 1 , wherein preparation of the mixed liquid is performed by preparing an aqueous dispersion of the cellulose nanofibers in which the cellulose nanofibers are dispersed in water, and then adding the organic solvent to the aqueous dispersion of the cellulose nanofibers.
3. The method of producing a porous cellulose body according to claim 1 , wherein the number average fiber diameter of the cellulose nanofibers is 1 to 100 nm.
4. The method of producing a porous cellulose body according to claim 1 , wherein the organic solvent comprises at least one product selected from the group consisting of: alcohols, carboxylic acids and carbonyl compounds.
5. The method of producing a porous cellulose body according to claim 4 , wherein the organic solvent comprises at least one product selected from the group consisting of: methanol, ethanol, 2-propanol, t-butyl alcohol as the alcohols, acetic acid as the carboxylic acids and acetone as the carbonyl compounds.
6. The method of producing a porous cellulose body according to claim 1 , wherein the organic solvent is t-butyl alcohol alone.
7. A porous cellulose body obtained with the method of producing a porous cellulose body according to claim 1 , wherein
the specific surface area by a nitrogen adsorption BET method is 70 m 2 /g or more.
8. The porous cellulose body according to claim 7 , the porous cellulose body being attached to the surface, or the surface and the inside of a porous support.
9. The method of producing a porous cellulose body according to claim 2 , wherein the number average fiber diameter of the cellulose nanofibers is 1 to 100 nm.
10. The method of producing a porous cellulose body according to claim 2 , wherein the organic solvent comprises at least one product selected from the group consisting of: alcohols, carboxylic acids and carbonyl compounds.
11. The method of producing a porous cellulose body according to claim 10 , wherein the organic solvent comprises at least one product selected from the group consisting of: methanol, ethanol, 2-propanol, t-butyl alcohol as the alcohols, acetic acid as the carboxylic acids, and acetone as the carbonyl compounds.
12. The method of producing a porous cellulose body according to claim 3 , wherein the organic solvent comprises at least one product selected from the group consisting of: alcohols, carboxylic acids and carbonyl compounds.
13. The method of producing a porous cellulose body according to claim 12 , wherein the organic solvent comprises at least one product selected from the group consisting of: methanol, ethanol, 2-propanol, t-butyl alcohol as the alcohols, acetic acid as the carboxylic acids and acetone as the carbonyl compounds.
14. The method of producing a porous cellulose body according to claim 2 , wherein the organic solvent is t-butyl alcohol alone.
15. The method of producing a porous cellulose body according to claim 3 , wherein the organic solvent is t-butyl alcohol alone.
16. A porous cellulose body obtained with the method of producing a porous cellulose body according to claim 2 , wherein
the specific surface area by a nitrogen adsorption BET method is 70 m 2 /g or more.
17. The porous cellulose body according to claim 16 , the porous cellulose body being attached to the surface, or the surface and the inside of a porous support.