Method for stabilizing beta-hemihydrate plaster
The instant invention is concerned with the post-treatment of β-hemihydrate plasters for the purpose of stabilization. The invention relies in the addition of a retardant to the calcined β-hemihydrate. It is also the purpose of the invention to provide stabilized β-hemihydrate plasters which exhibit advantageous properties.
1. A process for the manufacture of stabilized β-hemihydrate plaster powder comprising the moistening of calcined β-Hemihydrate with the addition of a retardant.
2. The process according to claim 1 , comprising the steps of
providing calcined β-hemihydrate plaster; and
moistening of said calcined β-Hemihydrate by the addition of water and a retardant to provide stabilized -hemihydrate plaster powder, the amount of moistening water is comprised between 1 and 6% by weight based on the weight of the fed-hemihydrate plaster.
3. The process according to claim 1 , wherein the retardant is added together with the moistening water.
4. The process according to claim 1 , wherein the amount of residual water in the stabilized β-hemihydrate plaster powder is less than 3.5%, by weight pursuant to standard ASTM C471 M.
5. The process according to claim 1 , wherein the amount of residual water in the stabilized 13 -hemihydrate plaster powder is less than 2.6%, by weight pursuant to standard ASTM C471 M.
6. The process according to claim 1 , wherein the amount of residual water in the stabilized β-hemihydrate plaster powder is less than 2.2%, by weight pursuant to standard ASTM C471 M.
7. The process according to claim 1 , wherein the amount of residual water in the stabilized β-hemihydrate plaster powder is less than 1.8%, by weight pursuant to standard ASTM C471 M.
8. The process according to claim 1 , wherein the amount of water is comprised between 1 and 6% by weight based on the weight of the fed β-hemihydrate plaster.
9. The process according to claim 1 , wherein the amount of water is comprised between 3 and 5% by weight based on the weight of the fed β-hemihydrate plaster.
10. The process according to claim 1 , wherein the amount of retardant is from 0.001 to 0.1% by weight based on the weight of the fed β-hemihydrate plaster.
11. The process according to claim 1 , wherein the amount of retardant is from 0.005 to 0.1% by weight based on the weight of the fed β-hemihydrate plaster.
12. The process according to claim 1 , wherein the amount of retardant is from 0.01 to 0.03% by weight based on the weight of the fed β-hemihydrate plaster.
13. The process according to claim 1 , wherein the retardant is selected from the group consisting of nucleation retardants, hydrolysed or degraded proteins, hydrolysed amino acid, polycondensated amino acid, phosphonic acids and salts thereof, polyphosphoric acid, phosphates and salts thereof, carboxylic acids in basic pH, polyacrylic acids having a molecular weight of less than 5000, and mixtures thereof.
14. The process according to claim 1 , wherein the retardant is a hydrolysed amino acid or a mixture thereof.
15. The process according to claim 14 , wherein the hydrolysed amino acid is selected from the group consisting of polycondensated amino acid, Ca-salt, polycondensated amino acid Ca-salt as a liquid solution, degraded mixture of polyamides, salified with calcium, modified amino acid or mixture thereof.
16. The process according to claim 1 , wherein the β-hemihydrate plaster fed into the process has a temperature comprised between 10° C. and 99° C.
17. The process according to claim 1 , wherein the β-hemihydrate plaster fed into the process has a temperature comprised between 25° C. and 80° C.
18. The process according to claim 1 , wherein the β-hemihydrate plaster fed into the process has a temperature comprised between 25° C. and 60° C.
19. The process according to claim 1 , carried out at atmospheric pressure.
20. The process according to claim 1 wherein the stabilized β-hemihydrate plaster is further subjected to a drying and/or grinding step and optionally stored for at least several days before being subjected to a drying and/or grinding step.
21. The process according to claim 20 , wherein the drying step is performed at a temperature within the range of 75 and 130° C.
22. The process according to claim 20 , wherein the drying step is performed at a temperature within the range of 75 to 115° C.
23. The process according to claim 20 , wherein the drying step is performed at a temperature within the range of 75 to 105° C.