Three-piece can and method of manufacturing the same
A three-piece can includes a can body obtained by forming a steel sheet such that a roundness of the can is 0.34 mm or less. The steel sheet contains: by mass %, C: 0.020% or more and 0.100% or less; Si: 0.10% or less; Mn: 0.10% or more and 0.80% or less; P: 0.001% or more and 0.100% or less; S: 0.001% or more and 0.020% or less; Al: 0.005% or more and 0.100% or less; and N: 0.0130% or more and 0.0200% or less. The balance is Fe and inevitable impurities. The steel sheet has a yield strength of 440 MPa or more and a total elongation of 12% or more.
1. A three-piece can comprising:
a can body obtained by forming a steel sheet having a yield strength, after performing a heat treatment at 210° C. for 10 minutes, of 440 MPa or more and 490 MPa or less and a total elongation, after performing the heat treatment at 210° C. for 10 minutes, of 12% or more such that a roundness of the can as measured according to JIS B 0621 and JIS B 0021 is 0.34 mm or less, the steel sheet containing: by mass %,
C: 0.020% or more and 0.100% or less;
Si: 0.10% or less;
Mn: 0.10% or more and 0.80% or less;
P: 0.001% or more and 0.100% or less;
S: 0.001% or more and 0.020% or less;
Al: 0.005% or more and 0.100% or less; and
N: 0.0130% or more and 0.0200% or less,
the balance being Fe and inevitable impurities.
2. A method of manufacturing a three-piece can comprising:
forming a steel sheet having a yield strength, after performing a heat treatment at 210° C. for 10 minutes, of 440 MPa or more and 490 MPa or less and a total elongation, after performing the heat treatment at 210° C. for 10 minutes, of 12% or more into a can body such that a roundness of the can as measured according to JIS B 0621 and JIS B 0021 is 0.34 mm or less, the steel sheet containing: by mass %,
C: 0.020% or more and 0.100% or less;
Si: 0.10% or less;
Mn: 0.10% or more and 0.80% or less;
P: 0.001% or more and 0.100% or less;
S: 0.001% or more and 0.020% or less;
Al: 0.005% or more and 0.100% or less; and
N: 0.0130% or more and 0.0200% or less,
the balance being Fe and inevitable impurities.