Optimized universal ion-selective electrode
The present invention relates to universal ion-selective electrode optimized for determinations of organic molecules. As opposed to the state of the art only one electrode composition is applicable to a variety of organic ions and ionizable molecules. It is accordingly an object of the present invention to provide an ISE composition that is optimized for the universal detection and determination of a very wide range of organic ions an ionizable organic molecules. As opposed to the state of the art this composition allows fast and sensitive detection of a very wide range of molecules independent of their chemical structure, class or number of charges. This optimized sensor can be used in different methodologies, e.g.: direct potentiometrie, standard addition, inline measurements and titration.
1. A method of making an ion-selective electrode for detecting organic ions and ionisable organic molecules comprising:
providing a Mesamoll plasticizer in an ion-selective polymeric matrix comprising 32% by weight of a Poly(vinylchloride) polymer, 65% by weight of said plasticizer, 2% by weight of an ionophoric potassium tetrakis (4-chlorophenyl)borate molecule and comprising one or more conductivity increasing salts, wherein said ion-selective polymeric matrix is sensitive to organic ions and ionisable organic molecules with logP values above 0, wherein said ion-selective polymeric matrix is not preloaded with said organic ions or said ionisable organic molecules with logP values above 0; and
incorporating said ion-selective polymeric matrix in the ion selective electrode.
2. The method according to claim 1 , wherein said conductivity increasing salts are present in an amount up to 20% by weight.
3. The method according to claim 1 , wherein the polymeric matrix further comprises electrically conducting particles.
4. The method according to claim 3 , wherein the electrically conducting particles are selected from the group consisting of gold, silver, glassy carbon, graphite, and carbon nanotubes.
5. The method according to claim 3 , wherein the polymeric matrix comprises a gradient of the electrically conducting particles which increases in concentration away from a sample contact surface.
6. The method according to claim 1 , wherein the polymeric matrix comprises a gradient of the ionophore potassium tetrakis (4-chlorophenyl)borate molecule which increases in concentration towards a sample contact surface.
7. The method according to claim 1 , wherein:
the conductivity increasing salts are lipophilic, and
the conductivity increasing salts are selected from the group consisting of tetradodecylammonium tetrakis(4-chlorophenyl)borate (ETH 500) and borates (BR 4 − ).
8. A wide range ion-selective polymeric matrix comprising 32% by weight of a Poly(vinylchloride) polymer, 65% by weight of a Mesamoll plasticizer, 2% by weight of an ionophoric potassium tetrakis (4-chlorophenyl)borate molecule and comprising one or more conductivity increasing salts, wherein said ion-selective polymeric matrix is sensitive to organic ions and ionisable organic molecules with logP values above 0, wherein said ion-selective polymeric matrix is not preloaded with said organic ions or said ionisable organic molecules with logP values above 0.
9. The wide range ion-selective polymeric matrix according to claim 8 , wherein said conductivity increasing salts are present in an amount up to 20% by weight.
10. The wide range ion-selective polymeric matrix according to claim 8 , wherein the polymeric matrix further comprises electrically conducting particles.
11. The wide range ion-selective polymeric matrix according to claim 10 , wherein the electrically conducting particles are selected from the group consisting of gold, silver, glassy carbon, graphite, and carbon nanotubes.
12. A potentiometric electrode comprising the wide range ion-selective polymeric matrix according to claim 8 .
13. The wide range ion-selective polymeric matrix according to claim 10 , wherein the polymeric matrix comprises a gradient of the electrically conducting particles which increases in concentration away from a sample contact surface.
14. The wide range ion-selective polymeric matrix according to claim 8 , wherein the polymeric matrix comprises a gradient of the ionophoric potassium tetrakis (4-chlorophenyl)borate molecule which increases in concentration towards a sample contact surface.
15. The wide range ion-selective polymeric matrix according to claim 8 , wherein:
the conductivity increasing salts are lipophilic, and
the conductivity increasing salts are selected from the group consisting of tetradodecylammonium tetrakis(4-chlorophenyl)borate (ETH 500) and borates (BR 4 − ).