Polymers grafted with organic phosphorous compounds for extracting uranium from solutions
Complexing or chelating agents that offer strong, selective bonding with uranium as well as a broad pH range of effectiveness, specifically including the pH range around 8.2, together with the acrylic double bonds required for radiation-induced grafting on polymers to remove uranium from a solution such as seawater. The novel adsorbing species are phosphorus-containing molecules, in particular organic phosphates, phosphonates and phosphoric acids. Organic phosphorus compounds, for example, organic phosphates, phosphonates, and phosphoric acids, are attached to polymer fibers to form fibers, fiber fabrics or membranes that are effective, or show activity, in uranium adsorption.
1. An adsorbent material prepared by a process of radiation grafting by using a source of ionizing radiation to graft bis(2-methacryloxyethyl) phosphate onto a polymeric fiber, while the polymeric fiber is immersed in an oxygen-free solution of the phosphate, wherein the polymeric fiber has a surface area of at least 10 m 2 /gram.
2. The adsorbent material according to claim 1 , wherein the radiation grafting bis(2-methacryloxyethyl) phosphate onto a polymeric fiber having a surface area of at least 10 m 2 /gram is performed by radiation grafting bis(2-methacryloxyethyl) phosphate onto polycaproamide.
3. The adsorbent material according to claim 1 , wherein the source of ionizing radiation is a gamma source providing a total radiation dose of 0.2-50 kGy to effect the grafting.
4. The adsorbent material according to claim 3 , wherein the gamma source provides a total radiation dose of 1-10 kGy to effect the grafting.
5. The adsorbent material according to claim 1 , wherein the polymeric fiber is irradiated while immersed in an oxygen-free solution containing components selected from the group consisting of surfactants, polar organic liquids, and combinations thereof.
6. The adsorbent material according to claim 1 , wherein the radiation grafting is characterized by a degree of grafting, defined as the weight gain of the polymeric fiber upon grafting and drying relative to its original weight, that is between 25% and 250%.
7. The adsorbent material according to claim 6 , wherein the degree of radiation grafting is between 50% and 200%.
8. The adsorbent material according to claim 7 , wherein the degree of radiation grafting is between 80% and 150%.
9. The adsorbent material according to claim 1 , wherein the polymer is sonicated following radiation grafting to remove homopolymerized material.
10. An adsorbent material prepared by a process of radiation grafting by using a source of ionizing radiation to graft bis(2-methacryloxyethyl) phosphate onto a polymer while the polymer is immersed in an oxygen-free solution of the phosphate, wherein the adsorbent material, consisting of the grafted polymer, is contacted with the aqueous solution, wherein the aqueous solution includes uranium, and the adsorbent material removes an amount of uranium, at least 0.1%, relative to the dry weight of the polymer, from the aqueous solution.
11. The adsorbent material according to claim 10 , wherein the adsorbent material is regenerated through desorption of the uranium using an aqueous solution to remove the uranium from the phosphate-grafted polymer.
12. The adsorbent material according to claim 11 , wherein the adsorbent material is regenerated through desorption of the uranium using a near-neutral solution of a complexing reagent to remove the uranium from the phosphate-grafted polymer.
13. The adsorbent material according to claim 12 , wherein the adsorbent material is regenerated through desorption of the uranium using a near-neutral solution of a complexing reagent that is an aqueous solution of ammonium oxalate to remove the uranium from the phosphate-grafted polymer.
14. A method of removing uranium from an aqueous solution comprising the steps of:
providing an adsorbent material produced by using a source of ionizing radiation to graft bis(2-methacryloxyethyl) phosphate onto a polymer; and
contacting the grafted polymer with the aqueous solution that includes uranium such that the adsorbent material removes an amount of uranium, at least 0.1%, relative to the dry weight of the polymer, from the aqueous solution.
15. The method of removing uranium from an aqueous solution according to claim 14 , wherein the radiation grafting of bis(2-methacryloxyethyl) phosphate onto the polymer is performed by radiation grafting bis(2-methacryloxyethyl) phosphate onto a polymeric fiber having a surface area of at least 10 m 2 /gram.
16. The method of removing uranium from an aqueous solution according to claim 15 , wherein the radiation grafting bis(2-methacryloxyethyl) phosphate onto the polymeric fiber having a surface area of at least 10 m 2 /gram is performed by radiation grafting bis(2-methacryloxyethyl) phosphate onto polycaproamide.
17. The method of removing uranium from an aqueous solution according to claim 14 , wherein the source of ionizing radiation is a gamma source providing a total radiation dose of 0.2-50 kGy to effect the radiation grafting.
18. The method of removing uranium from an aqueous solution according to claim 17 , wherein the gamma source provides a total radiation dose of 1-10 kGy to effect the radiation grafting.
19. The method of removing uranium from an aqueous solution according to claim 14 , wherein the step of contacting the grafted polymer with the aqueous solution includes contacting the grafted polymer with a solution containing components selected from the group consisting of surfactants, polar organic liquids, and combinations thereof.
20. The method of removing uranium from an aqueous solution according to claim 14 , wherein the radiation grafting is characterized by a degree of grafting, defined as the weight gain of the polymer upon grafting and drying relative to its original weight, that is between 25% and 250%.
21. The method of removing uranium from an aqueous solution according to claim 20 , wherein the degree of radiation grafting is between 50% and 200%.
22. The method of removing uranium from an aqueous solution according to claim 21 , wherein the degree of radiation grafting is between 80% and 150%.
23. The method of removing uranium from an aqueous solution according to claim 14 , wherein the polymer is sonicated following radiation grafting to remove homopolymerized material.
24. The method of removing uranium from an aqueous solution according to claim 14 , wherein the adsorbent material is regenerated through desorption of the uranium using an aqueous solution to remove the uranium from the phosphate-grafted polymer.
25. The method of removing uranium from an aqueous solution according to claim 24 , wherein the adsorbent material is regenerated through desorption of the uranium using a near-neutral solution of a complexing reagent to remove the uranium from the phosphate-grafted polymer.
26. The method of removing uranium from an aqueous solution according to claim 25 , wherein the adsorbent material is regenerated through desorption of the uranium using a near-neutral solution of a complexing reagent that is an aqueous solution of ammonium oxalate to remove the uranium from the phosphate-grafted polymer.
27. An adsorbent material for removing uranium from an aqueous solution
wherein the adsorbent material is prepared by a process of radiation grafting by using a source of ionizing radiation to graft bis(2-methacryloxyethyl) phosphate onto a polymer, while the polymer is immersed in an oxygen-free solution of the organic phosphate;
contacting the grafted polymer with the aqueous solution that includes uranium such that the adsorbent material removes an amount of uranium, at least 0.1%, relative to the dry weight of the polymer, from the aqueous solution; and
regenerating the adsorbent material at least once through desorption of the uranium using a near-neutral solution of a complexing reagent that is an aqueous solution of ammonium oxalate to remove the uranium from the phosphate-grafted polymer.
28. The adsorbent material according to claim 27 , wherein the adsorbent material for removing uranium from an aqueous solution is an adsorbent material for removing uranium from an aqueous solution of one of brine or seawater.
29. The adsorbent material according to claim 27 , wherein the radiation grafting of bis(2-methacryloxyethyl) phosphate onto the polymer is performed by radiation grafting bis(2-methacryloxyethyl) phosphate onto a polymeric fiber having a surface area of at least 10 m 2 /gram.
30. The adsorbent material according to claim 29 , wherein the radiation grafting bis(2-methacryloxyethyl) phosphate onto a polymeric fiber having a surface area of at least 10 m 2 /gram is performed by radiation grafting bis(2-methacryloxyethyl) phosphate onto polycaproamide.
31. The adsorbent material according to claim 27 , wherein the source of ionizing radiation is a gamma source providing a total radiation dose of 0.2-50 kGy to effect the grafting.
32. The adsorbent material according to claim 31 , wherein the gamma source provides a total radiation dose of 1-10 kGy to effect the grafting.
33. The adsorbent material according to claim 27 , wherein the radiation grafting is performed with the polymer first irradiated in the absence of oxygen and then contacted with an oxygen-free solution of the organic phosphate.
34. The adsorbent material according to claim 27 , wherein the radiation grafting is performed with the polymer irradiated while immersed in an oxygen-free solution of the organic phosphate.
35. The adsorbent material according to claim 27 , wherein the polymer is irradiated while immersed in an oxygen-free solution containing components selected from the group consisting of surfactants, polar organic liquids, and combinations thereof.
36. The adsorbent material according to claim 27 , wherein the radiation grafting is characterized by a degree of grafting, defined as the weight gain of the polymer upon grafting and drying relative to its original weight, that is between 25% and 250%.
37. The adsorbent material according to claim 36 , wherein the degree of radiation grafting is between 50% and 200%.
38. The adsorbent material according to claim 37 , wherein the degree of radiation grafting is between 80% and 150%.
39. The adsorbent material according to claim 27 , wherein the polymer is sonicated following radiation grafting to remove homopolymerized material.
40. A method of removing uranium from an aqueous solution comprising the steps of:
providing an adsorbent material produced by using a source of ionizing radiation to graft bis(2-methacryloxyethyl) phosphate onto a polymer;
contacting the grafted polymer with the aqueous solution that includes uranium such that the adsorbent material removes an amount of uranium, at least 0.1%, relative to the dry weight of the polymer, from the aqueous solution; and
regenerating the adsorbent material at least once through desorption of the uranium using a near-neutral solution of a complexing reagent that is an aqueous solution of ammonium oxalate to remove the uranium from the phosphate-grafted polymer.
41. The method of removing uranium from an aqueous solution according to claim 40 , wherein the adsorbent material removes uranium from an aqueous solution that is one of brine or seawater.
42. The method of removing uranium from an aqueous solution according to claim 40 , wherein, following adsorption of uranium from the aqueous solution followed by regeneration with an aqueous solution of ammonium oxalate, the distribution coefficient of the regenerated adsorbent material is greater than 250.
43. The method of removing uranium from an aqueous solution according to claim 42 , wherein the distribution coefficient of the regenerated adsorbent material is greater than 500.
44. The method of removing uranium from an aqueous solution according to claim 40 , wherein, following at least 15 cycles of adsorption of uranium from the aqueous solution followed by regeneration with an aqueous solution of ammonium oxalate, the distribution coefficient of the regenerated adsorbent material is greater than 250.
45. The method of removing uranium from an aqueous solution according to claim 44 , wherein the distribution coefficient of the regenerated adsorbent material is greater than 500.
46. The method of removing uranium from an aqueous solution according to claim 41 , wherein, following at least 15 cycles of adsorption of uranium from the brine or seawater followed by regeneration with an aqueous solution of ammonium oxalate, the distribution coefficient of the regenerated adsorbent material is greater than 250.
47. The method of removing uranium from an aqueous solution according to claim 46 , wherein the distribution coefficient of the regenerated adsorbent material is greater than 500.
48. The method of removing uranium from an aqueous solution according to claim 41 , wherein, following at least 15 cycles of adsorption of uranium from the brine or seawater followed by regeneration with an aqueous solution of ammonium oxalate, the distribution coefficient of the regenerated adsorbent material is greater than 250.
49. The method of removing uranium from an aqueous solution according to claim 48 , wherein the distribution coefficient of the regenerated adsorbent material is greater than 500.
50. The method of removing uranium from an aqueous solution according to claim 40 , wherein the radiation grafting of bis(2-methacryloxyethyl) phosphate onto the polymer is performed by radiation grafting bis(2-methacryloxyethyl) phosphate onto a polymeric fiber having a surface area of at least 10 m 2 /gram.
51. The method of removing uranium from an aqueous solution according to claim 50 , wherein the radiation grafting bis(2-methacryloxyethyl) phosphate onto the polymeric fiber having a surface area of at least 10 m 2 /gram is performed by radiation grafting bis(2-methacryloxyethyl) phosphate onto polycaproamide.
52. The method of removing uranium from an aqueous solution according to claim 40 , wherein the source of ionizing radiation is a gamma source providing a total radiation dose of 0.2-50 kGy to effect the radiation grafting.
53. The method of removing uranium from an aqueous solution according to claim 52 , wherein the gamma source provides a total radiation dose of 1-10 kGy to effect the radiation grafting.
54. The method of removing uranium from an aqueous solution according to claim 40 , wherein the radiation grafting is performed with the polymer first irradiated in the absence of oxygen and then contacted with an oxygen-free solution of the organic phosphate.
55. The method of removing dissolved uranium from an aqueous solution according to claim 40 , wherein the radiation grafting is performed with the polymer irradiated while immersed in an oxygen-free solution of the organic phosphate.
56. The method of removing uranium from an aqueous solution according to claim 40 , wherein the step of contacting the grafted polymer with the aqueous solution includes contacting the grafted polymer with a solution containing components selected from the group consisting of surfactants, polar organic liquids, and combinations thereof.
57. The method of removing uranium from an aqueous solution according to claim 40 , wherein the radiation grafting is characterized by a degree of grafting, defined as the weight gain of the polymer upon grafting and drying relative to its original weight, that is between 25% and 250%.
58. The method of removing uranium from an aqueous solution according to claim 57 , wherein the degree of radiation grafting is between 50% and 200%.
59. The method of removing uranium from an aqueous solution according to claim 58 , wherein the degree of radiation grafting is between 80% and 150%.
60. The method of removing uranium from an aqueous solution according to claim 40 , wherein the polymer is sonicated following radiation grafting to remove homopolymerized material.