Redox flow cell comprising high molecular weight compounds as redox pair and semipermeable membrane for storage of electrical energy
It was an object of the invention to provide, by use of new materials and membranes and with very little outlay, an inexpensive and long-lived redox flow cell which even in the event of a possible serious accident brings about little environmental pollution by its redox-active compounds. According to the invention, high molecular weight compounds such as redox-active polymers or oligomers are provided as redox-active components and a size-exclusion membrane ( 3 ) is provided as membrane for the separation of the high molecular weight redox-active components.
1. A redox flow cell for storage of electric energy, containing a reaction cell having two polarity-specific chambers ( 1 , 2 ) for catholyte and anolyte, which are each connected to a store for liquid and are separated by a membrane for ion exchange, where the chambers ( 1 , 2 ) are each filled with redox-active components present undiluted, in dissolved form or dispersed in an electrolyte solvent and also conducting salts dissolved therein and optionally further additives, characterized in that high molecular weight compounds are provided as redox-active components and a size-exclusion membrane ( 3 ) is provided as membrane for separating the high molecular weight redox-active components present undiluted, in dissolved form or in dispersed form, wherein the high molecular weight redox-active components comprise polymers containing groups which form nitroxide radicals, verdazyl radicals or nitronylnitroxide radicals, viologens or quinones.
2. The redox flow cell as claimed in claim 1 , characterized in that the chambers ( 1 , 2 ) are each filled with redox-active components which are present undiluted or as a solution in water or an organic solvent.
3. The redox flow cell as claimed in claim 1 , characterized in that a semipermeable membrane is provided as size-exclusion membrane.
4. The redox flow cell as claimed in claim 1 , characterized in that a dialysis membrane is provided as size-exclusion membrane.
5. The redox flow cell as claimed in claim 1 , characterized in that the size-exclusion membrane has a selectivity of at least 500 g/mol and the high molecular weight redox-active components have a corresponding molar mass of greater than 500 g/mol.
6. The redox flow cell as claimed in claim 1 , characterized in that the size-exclusion membrane consists of plastics, ceramics, glasses, metals, composites or sheet-like textile structures or combinations thereof.
7. The redox flow cell as claimed in claim 1 , characterized in that the size-exclusion membrane consists of organic material and is, in particular, configured as polymer membrane.
8. The redox flow cell as claimed in claim 1 , characterized in that the thickness of the size-exclusion membrane is in the range from 1 μm to 5 mm.
9. The redox flow cell as claimed in claim 1 , characterized in that the high molecular weight redox-active component polymers have a polymer backbone selected from the group consisting of polymethacrylates, polyacrylates, polystyrenes, polyalkylene glycols and polyvinyl ethers and have redox-active components selected from the group consisting of groups which form nitroxide radicals, verdazyl radicals or nitronylnitroxide radicals, viologens and quinones covalently bound to the polymer backbone.
10. The redox flow cell as claimed in claim 1 , characterized in that the redox-active component polymers are present as linear polymers or as branched polymers.
11. The redox flow cell as claimed in claim 1 , characterized in that the viscosity of the electrolytes used is in the range from 1 mPas to 10 6 mPas, measured at 25° C. using a rotational viscometer, plate/plate.
12. A method for the storage of electric energy for mobile and stationary applications comprising utilizing a redox flow cell as claimed in claim 1 .
13. The method as claimed in claim 12 , characterized in that the redox flow cell is utilized in the field of electromobility, as electrical energy storage in land, air and water vehicles, or in that the redox flow cell is utilized as stationary electrical energy storage for emergency power supply, peak load equalization and for the temporary storage of electric energy from renewable energy sources, in particular in the sector of photovoltaics and wind power.
14. The redox flow cell as claimed in claim 5 , characterized in that the size-exclusion membrane has a selectivity of at least 500 g/mol and the high molecular weight redox-active components have a corresponding molar mass of greater than or equal to 550 g/mol.
15. The redox flow cell as claimed in claim 6 , characterized in that the size-exclusion membrane consists of organic polymers selected from cellulose or modified cellulose, polyether sulfone, polysulfone, polyvinylidene fluoride, polyesters, polyurethanes, polyamides, polypropylene, polyvinyl chloride, polyacrylonitrile, dextran, lignin, polypropylene oxide, polyethylenimine, polyacrylic acid, polystyrene, polyvinyl alcohol, polyphenylene oxide, polyimides, polytetrafluoroethylene or derivatives thereof.
16. The redox flow cell as claimed in claim 8 , characterized in that the thickness of the size-exclusion membrane is in the range from 10 μm to 200 μm.
17. The redox flow cell as claimed in claim 10 , characterized in that the redox-active component polymers which are present as linear polymers or as branched polymers are selected from the group consisting of comb or star polymers, dendrimers, conductive polymers, cyclic polymers, polycatenanes and polyrotaxanes.
18. The redox flow cell as claimed in claim 1 , characterized in that the viscosity of the electrolytes used is in the range from 10 2 to 10 4 mPas, measured at 25° C. using a rotational viscometer, plate/plate.