Separator and method of preparing the same, and lithium ion secondary battery
An object of the present invention is to provide a separator maintaining high rate characteristics and enabling suppression of short circuit. The object is achieved by a separator comprising a substrate having an inner surface and an outer surface, and inorganic particles presented on the outer surface and the inner surface of the substrate, wherein the substrate has a porosity of 55% or more and a mean flow pore size of 30 μm or less, the inorganic particles have an average particle size of 1.0 to 4.0 μm, and the inorganic particles comprises 40% by volume or less of particles having a particle size of 1.0 μm or less and 30 to 75% by volume of particles having a particle size of 2.0 μm or more.
1. A separator comprising a substrate having an inner surface and an outer surface, and inorganic particles present on the outer surface and the inner surface of the substrate,
wherein the substrate has a porosity of 55% or more and a mean flow pore size of 30 μm or less and comprises nonwoven fabric that has a coefficient of texture variation of 1.7 or less and a total basis weight of 5 to 15 g/m 2 ,
the inorganic particles have an average particle size of 1.0 to 4.0 μm, and the inorganic particles comprise 40% by volume or less of particles having a particle size of 1.0 μm or less and 30 to 75% by volume of particles having a particle size of 2.0 μm or more.
2. The separator according to claim 1 , wherein the substrate comprises a nonwoven fabric containing one or more resins selected from the group consisting of polyolefin-based resins and polyester-based resins.
3. The separator according to claim 2 , wherein the substrate comprises a laminated nonwoven fabric comprising a first nonwoven fabric layer comprising fibers having a fiber diameter of 4.0 μm or less and a second nonwoven fabric layer comprising fibers having a fiber diameter of more than 4.0 μm and 30.0 μm or less.
4. The separator according to claim 1 , further comprising 4 parts by mass or more of a binder based on 100 parts by mass of the inorganic particles, the binder being present inside the substrate.
5. A separator comprising a substrate having an inner surface and an outer surface, and inorganic particles present on the outer surface and the inner surface of the substrate,
wherein the substrate comprises a laminated nonwoven fabric formed by laminating a plurality of nonwoven fabric layers,
the laminated nonwoven fabric has a coefficient of texture variation of 1.7 or less and a total basis weight of 5 to 15 g/m 2 , and
the separator has a porosity of 45 to 70%,
a pore size distribution of the separator has one or more local maximum values in the range of a pore size of 0.1 to 1 μm and one or more local maximum values in the range of a pore size of 1 to 10 μm.
6. A method of preparing the separator according to claim 1 , the method comprising the steps of:
dispersing inorganic particles in a dispersive medium to prepare a slurry,
applying the slurry to a substrate or impregnating a substrate with the slurry to prepare a substrate with the slurry, and
drying the substrate with the slurry,
wherein the substrate has a porosity of 55% or more and a mean flow pore size of 30 μm or less,
the inorganic particles have the average particle size of 1.0 to 4.0 μm or less, and the inorganic particles comprise 40% by volume or less of particles having a particle size of 1.0 μm or less and 30 to 75% by volume of particles having a particle size of 2.0 μm or more.
7. The separator according to claim 1 , wherein the inorganic particles have a plate-like shape.
8. The separator according to claim 1 , wherein the separator is used for an electrochemical element.
9. A lithium ion secondary battery, comprising a positive electrode, a negative electrode, an electrolytic solution, and the separator according to claim 1 .
10. The lithium ion secondary battery according to claim 9 , wherein the electrolytic solution comprises at least one compound selected from the group consisting of carbonate esters having carbon-carbon double bond, cyclic carbonates having a fluorine atom, and sulfones.
11. The lithium ion secondary battery according to claim 10 , wherein the carbonate esters having carbon-carbon double bond comprise vinylene carbonate, the cyclic carbonates having a fluorine atom comprise fluoroethylene carbonate, and the sulfones comprise sulfolane.
12. The separator according to claim 1 , wherein the nonwoven fabric is a laminated nonwoven fabric comprising a nonwoven fabric layer (I) and a nonwoven fabric layer (II), wherein
the nonwoven fabric layer (I) contains 50% or more of microfibers having a fiber diameter from 0.3 μm to 4 μm, and
the nonwoven fabric layer (II) contains fibers having a fiber diameter of more than 4.0 μm and 30.0 μm or less.