Method for storing episulfide compound and method for preparing thioepoxy-based optical material using said episulfide compound
Disclosed is a method of storing a thioepoxy compound and a method of preparing a thioepoxy based optical material using the thioepoxy compound. Particularly, a method of preparing a high-quality thioepoxy based optical material having superior color and thermal stability and less time-dependent change, and being colorless and transparent by inhibiting time-dependent change of the thioepoxy compound during storage is disclosed. In addition, a method of storing the thioepoxy compound for an optical material, the thioepoxy compound having a water content of 500 to 2,500 ppm and stored at −78 to 10° C., and a method of preparing the thioepoxy based optical material, the method including polymerizing a polymerizable composition including the stored thioepoxy compound, are provided. The high-quality thioepoxy based optical material, which is colorless and transparent, prepared according to the present invention may be broadly used in a variety of fields as a substitute for conventional optical materials.
1. A method of storing a polythioepoxy compound for an optical material, the method comprising storing the polythioepoxy compound having a water content of 500 to 2,500 ppm at −78 to 10° C.
2. The method according to claim 1 , wherein the polythioepoxy compound is stored at −50 to 0° C.
3. The method according to claim 2 , wherein the water content is 600 to 1,500 ppm.
4. The method according to claim 1 , wherein the polythioepoxy compound is stored for 3 years or less.
5. A method of preparing a polythioepoxy based optical material, the method comprising polymerizing a polymerizable composition comprising the polythioepoxy compound having a water content of 500 to 2,500 ppm, stored at −78 to 10° C.
6. The method according to claim 5 , wherein the polymerizable composition further comprises a polyisocyanate compound.
7. The method according to claim 5 , wherein the polymerizable composition further comprises a polythiol compound.
8. The method according to claim 5 , wherein the polymerizable composition further comprises a polyisocyanate compound and a polythiol compound.
9. The method according to claim 5 , wherein the polythioepoxy compound is at least one compound selected from the group consisting of bis(2,3-epithiopropyl)sulfide, bis(2,3-epithiopropyl)disulfide, 1,3-bis(β-epithiopropylthio)cyclohexane, 1,4-bis(β-epithiopropylthio)cyclohexane, 1,3-bis(β-epithiopropylthiomethyl)cyclohexane, 1,4-bis(β-epithiopropylthiomethyl)cyclohexane, 2,5-bis(β-epithiopropylthiomethyl)-1,4-dithiane, 2,5-bis(β-epithiopropylthioethylthiomethyl)-1,4-dithiane, and 2-(2-β-epithiopropylthioethylthio)-1,3-bis(β-epithiopropylthio)propane.
10. A polythioepoxy based optical material prepared by the method according to claim 5 .
11. An optical lens composed of the polythioepoxy based optical material according to claim 10 .
12. The optical lens according to claim 11 , wherein the optical lens is an eyeglass lens or a polarizing lens.