IP Library › Granted Patent US 9,490,124
Granted Patent B2
US 9,490,124 · App. 14/433,656 · Granted Nov 8, 2016

Polycrystalline silicon substrate and manufacturing method thereof

Inventor: Lijuan Tang (Guangdong, CN)
Assignee: Shenzhen China Star Optoelectronics Technology Co., Ltd
H01L21/02672H01L21/0217H01L21/02126H01L21/02164H01L21/02532H01L21/02592H01L21/02694H01L21/2254H01L21/3247H01L29/04H01L29/16
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 9,490,124
App. No.
14/433,656
Granted
Nov 8, 2016
Kind
B2
Abstract

The present invention discloses a polycrystalline silicon substrate and a manufacturing method thereof. The method comprises: provide a substrate; sequentially form an amorphous silicon layer, an insulating layer and a metal catalyst layer; anneal the substrate at the first time, so that metal ions of the metal catalyst layer extend down to the amorphous silicon layer through the insulating layer, thereby inducing the amorphous silicon on the amorphous silicon layer to crystallize at the first time; remove the insulating layer and the metal catalyst layer; anneal the substrate at the second time, so that the metal ions lateral diffuse along the amorphous silicon layer, thereby inducing the amorphous silicon on the amorphous silicon layer to crystallize at the second time, forming the polycrystalline silicon layer. Through the above way, it can reduce the metal catalyst residues during forming the polycrystalline silicon layer, decreasing the leakage current of the semiconductor layer in the thin film transistor, thereby raising the performance of the thin film transistor.

Claims (43)

1. A manufacturing method of a polycrystalline silicon substrate, comprising:

providing a substrate;

sequentially forming an amorphous silicon layer, an insulating layer and a metal catalyst layer on the substrate;

conducting a first annealing operation at a first annealing temperature on the substrate so that metal ions of the metal catalyst layer extend down into amorphous silicon of a portion of the amorphous silicon layer through the insulating layer, thereby inducing primary crystallization in the amorphous silicon of the portion of the amorphous silicon layer to convert the amorphous silicon of the portion of the amorphous silicon layer into polycrystalline silicon;

removing the insulating layer and the metal catalyst layer; and

conducting a second annealing operation at a second annealing temperature on the substrate so that the metal ions extending into the portion of the amorphous silicon layer laterally diffuse along a remaining portion of the amorphous silicon layer, wherein the metal ions induce secondary crystallization in amorphous silicon of the remaining portion of the amorphous silicon layer to convert the amorphous silicon of the remaining portion of the amorphous silicon layer into polycrystalline silicone, thereby changing the amorphous silicon layer into a polycrystalline silicon layer, wherein the metal ions induce the secondary crystallization laterally along the remaining portion of the amorphous silicon layer to reach an end of the remaining portion and thus gathers at an end portion of the polycrystalline silicon layer that corresponds to the end of the remaining portion of the amorphous silicon layer;

wherein a step of patterning the metal catalyst layer is conducted before conducting a first annealing operation on the substrate; and

wherein a step of patterning the polycrystalline silicon layer is conducted after conducting a second annealing operation on the substrate in order to remove the end portion of the polycrystalline silicon layer and thus remove the metal ions gathering in the end portion of the polycrystalline silicon layer.

2. The manufacturing method as claimed in claim 1 , wherein a step of forming a buffer layer on the substrate is conducted before sequentially forming an amorphous silicon layer, an insulating layer and a metal catalyst layer on the substrate; and

the step of sequentially forming an amorphous silicon layer, an insulating layer and a metal catalyst layer on the substrate comprises:

forming the amorphous silicon layer, the insulating layer and the metal catalyst layer on the buffer layer.

3. A manufacturing method of a polycrystalline silicon substrate, comprising:

providing a substrate;

sequentially forming an amorphous silicon layer, an insulating layer and a metal catalyst layer on the substrate;

conducting a first annealing operation at a first annealing temperature on the substrate so that metal ions of the metal catalyst layer extend down into amorphous silicon of a portion of the amorphous silicon layer through the insulating layer, thereby inducing primary crystallization in the amorphous silicon of the portion of the amorphous silicon layer to convert the amorphous silicon of the portion of the amorphous silicon layer into polycrystalline silicon;

removing the insulating layer and the metal catalyst layer; and

conducting a second annealing operation at a second annealing temperature on the substrate so that the metal ions extending into the portion of the amorphous silicon layer laterally diffuse along a remaining portion of the amorphous silicon layer, wherein the metal ions induce secondary crystallization in amorphous silicon of the remaining portion of the amorphous silicon layer to convert the amorphous silicon of the remaining portion of the amorphous silicon layer into polycrystalline silicone, thereby changing the amorphous silicon layer into a polycrystalline silicon layer, wherein the metal ions induce the secondary crystallization laterally along the remaining portion of the amorphous silicon layer to reach an end of the remaining portion and thus gathers at an end portion of the polycrystalline silicon layer that corresponds to the end of the remaining portion of the amorphous silicon layer;

wherein a step of patterning the polycrystalline silicon layer is conducted after conducting a second annealing operation on the substrate in order to remove the end portion of the polycrystalline silicon layer and thus remove the metal ions gathering in the end portion of the polycrystalline silicon layer.

4. The manufacturing method as claimed in claim 3 , wherein the first annealing temperature is 500-600° C.

5. The manufacturing method as claimed in claim 3 , wherein the second annealing temperature is 500-600° C.

6. The manufacturing method as claimed in claim 3 , wherein a step of forming a buffer layer on the substrate is conducted before sequentially forming an amorphous silicon layer, an insulating layer and a metal catalyst layer fur on the substrate; and

the step of sequentially forming an amorphous silicon layer, an insulating layer and a metal catalyst layer on the substrate comprises:

forming the amorphous silicon layer, the insulating layer and the metal catalyst layer on the buffer layer.

7. The manufacturing method as claimed in claim 6 , wherein the buffer layer is formed of at least one of silicon oxide, silicon nitride and silicon oxynitride, or a combination thereof.

8. The manufacturing method as claimed in claim 3 , wherein the insulating layer is formed of at least one of silicon oxide, silicon nitride and silicon oxynitride, or a combination thereof.

9. The manufacturing method as claimed in claim 3 , wherein the metal catalyst layer is formed of at least one of Ni, Pd, Ti, Ag, Au, Al, Sn, Sb, Cr and Mo, or a combination thereof.

10. The manufacturing method as claimed in claim 3 , wherein a step of patterning the metal catalyst layer is conducted before conducting a first annealing operation on the substrate.

11. A polycrystalline silicon substrate, which is manufactured with the following steps:

providing a substrate;

sequentially forming an amorphous silicon layer, an insulating layer and a metal catalyst layer on the substrate;

conducting a first annealing operation at a first annealing temperature on the substrate so that metal ions of the metal catalyst layer extend down into amorphous silicon of a portion of the amorphous silicon layer through the insulating layer, thereby inducing primary crystallization in the amorphous silicon of the portion of the amorphous silicon layer to convert the amorphous silicon of the portion of the amorphous silicon layer into polycrystalline silicon;

removing the insulating layer and the metal catalyst layer; and

conducting a second annealing operation at a second annealing temperature on the substrate so that the metal ions extending into the portion of the amorphous silicon layer laterally diffuse along a remaining portion of the amorphous silicon layer, wherein the metal ions induce secondary crystallization in amorphous silicon of the remaining portion of the amorphous silicon layer to convert the amorphous silicon of the remaining portion of the amorphous silicon layer into polycrystalline silicone, thereby changing the amorphous silicon layer into a polycrystalline silicon layer, wherein the metal ions induce the secondary crystallization laterally along the remaining portion of the amorphous silicon layer to reach an end of the remaining portion and thus gathers at an end portion of the polycrystalline silicon layer that corresponds to the end of the remaining portion of the amorphous silicon layer;

wherein a step of patterning the polycrystalline silicon layer is conducted after conducting a second annealing operation on the substrate in order to remove the end portion of the polycrystalline silicon layer and thus remove the metal ions gathering in the end portion of the polycrystalline silicon layer.

12. The polycrystalline silicon substrate as claimed in claim 11 , wherein the first annealing temperature is 500−600° C.

13. The polycrystalline silicon substrate as claimed in claim 11 , wherein the second annealing temperature is 500−600° C.

14. The polycrystalline silicon substrate as claimed in claim 11 , wherein a step of forming a buffer layer on the substrate is conducted before sequentially forming an amorphous silicon layer, an insulating layer and a metal catalyst layer fur on the substrate; and

the step of sequentially forming an amorphous silicon layer, an insulating layer and a metal catalyst layer on the substrate comprises:

forming the amorphous silicon layer, the insulating layer and the metal catalyst layer on the buffer layer.

15. The polycrystalline silicon substrate as claimed in claim 14 , wherein the buffer layer is formed of at least one of silicon oxide, silicon nitride and silicon oxynitride, or a combination thereof.

16. The polycrystalline silicon substrate as claimed in claim 11 , wherein the insulating layer is formed of at least one of silicon oxide, silicon nitride and silicon oxynitride, or a combination thereof.

17. The polycrystalline silicon substrate as claimed in claim 11 , wherein the metal catalyst layer is formed of at least one of Ni, Pd, Ti, Ag, Au, Al, Sn, Sb, Cr and Mo, or a combination thereof.

18. The polycrystalline silicon substrate as claimed in claim 11 , wherein a step of patterning the metal catalyst layer is conducted before conducting a first annealing operation on the substrate.

Assignments (1)
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Apr 4, 2015
From: TANG, LIJUAN
To: SHENZHEN CHINA STAR OPTOELECTRONICS TECHNOLOGY CO., LTD.
Reel/Frame 035335/0233 →
Priority Claims (1)
CN 2014 1 0850901 · Dec 30, 2014 · national
Continuity (1)
Related Publication 20160189961A1 · Jun 30, 2016