Alumina-based fibrous mass, process for producing same, and use
To provide an alumina-based fibrous mass having a high areal pressure and is usable as a holding material for an exhaust gas cleaners and a production process thereof; the alumina-based fibrous mass has a chemical composition containing an Al 2 O 3 in an amount of 70% or more and less than 90% and having a total pore volume of 0.0055 mL/g or less.
1. A process for producing the alumina-based fibrous mass having a chemical composition comprising an Al 2 O 3 in an amount of 70 weight % or more and less than 90 weight % and having a total pore volume of 0.0055 mL/g or less, comprising: (I) a step in which an inorganic fiber source and a spinning aid are mixed together and concentrated under a reduced pressure to obtain a viscous spinning dope, (II) a step in which the spinning dope is extruded through fine holes into the air and dried to obtain a precursor, and (III) a step in which the precursor is burned, in this order, wherein,
the step of burning the precursor in said step (III) comprises
a degreasing step in which the burning is performed to 800° C. at a burning rate of 3° C./min or lower while performing evacuation at a rate of 0.1 to 3 Nm 3 /h per kg of the precursor, and
a crystallization step in which after the degreasing step, the inorganic fiber source is burned and crystallized.