Process for fabrication of enhanced β″-alumina solid electrolytes for energy storage devices and energy applications
A dense β″-alumina/zirconia composite solid electrolyte and process for fabrication are disclosed. The process allows fabrication at temperatures at or below 1600° C. The solid electrolytes include a dense composite matrix of β″-alumina and zirconia, and one or more transition metal oxides that aid the conversion and densification of precursor salts during sintering. The composite solid electrolytes find application in sodium energy storage devices and power-grid systems and devices for energy applications.
1. A fabrication process comprising:
(a)(1) calcining a mixture of Boehmite, zirconia or YSZ, Ti{OCH(CH 3 ) 2 } 4 , and Mn(NO 3 ) 2 ; or
(a)(2) calcining a mixture of Boehmite and Ti{OCH(CH 3 ) 2 } 4 , resulting in a first calcined product; separately calcining a mixture of YSZ and Mn(NO 3 ) 2 resulting in a second calcined product; and combining together the first calcined product and the second calcined product,
wherein the (a)(1) or (a)(2) calcining is performed at 400° C. to 900° C.; and
(b) sintering the (a)(1) calcined product or the (a)(2) combined calcined product in air at a temperature at or below about 1600° C. for a time selected to form a dense β″ alumina/zirconia or YSZ composite solid electrolyte.
2. The process of claim 1 , wherein the YSZ is doped with a quantity of yttrium at or below about 10 mol % by weight.
3. The process of claim 1 , wherein the ratio of Boehmite to zirconia or YSZ in the mixture prior to sintering is greater than about 50% by volume.
4. The process of claim 1 , wherein the ratio of Boehmite to zirconia or YSZ in the mixture prior to sintering is less than about 50% by volume.
5. The process of claim 1 , wherein the composite solid electrolyte includes a concentration of MnO 2 and TiO 2 at or below about 10% by weight on average.
6. The process of claim 1 , wherein the sintering is performed at a temperature between about 900° C. to about 1200° C.
7. The process of claim 1 , wherein the sintering is performed at a temperature between about 1200° C. to about 1500° C.
8. The process of claim 1 , wherein the composite solid electrolyte has a mechanical strength that is at least about 300 MPa.
9. The process of claim 1 , wherein the density of the composite solid electrolyte is greater than or equal to 98%.
10. The process of claim 1 , wherein the only source of aluminum is the Boehmite.
11. The process of claim 10 , wherein the YSZ is doped with a quantity of yttrium at or below about 10 mol % by weight.
12. The process of claim 10 , wherein the ratio of Boehmite to zirconia or YSZ in the mixture prior to sintering is greater than about 50% by volume.
13. The process of claim 10 , wherein the ratio of Boehmite to zirconia or YSZ in the mixture prior to sintering is less than about 50% by volume.
14. The process of claim 10 , wherein the composite solid electrolyte includes a concentration of MnO 2 and TiO 2 at or below about 10% by weight on average.
15. The process of claim 10 , wherein the (a)(1) or (a)(2) calcining mixture comprises at least one stabilizing metal salts.
16. The process of claim 15 , wherein the stabilizing metal salts comprises lithium salts, magnesium salts, or any combinations thereof.
17. The process of claim 1 , wherein the composite solid electrolyte further comprises Na.
18. The process of claim 17 , wherein the composite solid electrolyte includes a ratio of Na to Al of [1.67:10.67]; or [3.34:10.67]; or [4.18 to 10.67].
19. The process of claim 1 , wherein the Ti{OCH(CH 3 ) 2 } 4 , is present in the (a)(1) or (a)(2) calcining mixture at or below about 10 mol %.
20. The process of claim 1 , wherein the weight ratio of Boehmite:zirconia or Boehmite:YSZ in the mixture is about 7:3.
21. The process of claim 1 , wherein the (a)(1) or (a)(2) calcining mixture comprises at least one stabilizing metal salt.
22. The process of claim 21 , wherein the at least one stabilizing metal salt comprises lithium salts, magnesium salts, or any combinations thereof.
23. The process of claim 1 , wherein the Mn(NO 3 ) 2 is present in the (a)(1) or (a)(2) calcining mixture at or below about 10 mol %.
24. The process of claim 1 , wherein the (a)(1) calcining mixture further comprises NaNO 3 and LiNO 3 .
25. The process of claim 1 , wherein the composite solid electrolyte has a density greater than or equal to 97%.
26. The process of claim 1 , wherein the composite solid electrolyte has a density greater than or equal to 98%.
27. The process of claim 1 , wherein the composite solid electrolyte has a density greater than or equal to 99%.
28. The process of claim 1 , wherein the process includes the (a)(1) calcining.
29. The process of claim 1 , wherein the process includes the (a)(2) calcining.