Oxidation-resistant and wear-resistant polyethylenes for human joint replacements and methods for making them
The present invention presents methods for making oxidation-resistant and wear-resistant polyethylenes and medical implants made therefrom. Preferably, the implants are components of prosthetic joints, e.g., a bearing component of an artificial hip or knee joint. The resulting oxidation-resistant and wear-resistant polyethylenes and implants are also disclosed.
1. A method for producing a wear-resistant and oxidation-resistant medical implant for a joint prosthesis comprising:
providing an oxidation-resistant orthopaedic material comprising a polyethylene;
forming the orthopaedic material into an implant for the joint prosthesis;
packaging the orthopaedic material after being formed into the implant;
sterilizing the orthopaedic material while packaged; and
irradiating the orthopaedic material during the method at a total radiation dose of above 5 Mrad to about 25 Mrad so as to crosslink the orthopaedic material, thereby improving its wear resistance, without thermally treating the orthopaedic material to extinguish free radicals in the orthopaedic material during or subsequent to irradiating the orthopaedic material, wherein the orthopaedic material contains an antioxidant rendering it resistant to oxidation caused by free radicals generated by the irradiation.
2. The method of claim 1 , wherein the irradiated orthopaedic material possesses a degree of swelling of between about 1.7 to about 3.6.
3. The method of claim 1 , wherein the irradiated orthopaedic material possesses a molecular weight between crosslinks of between about 400 to about 3,500 g/mol.
4. The method of claim 1 , wherein the irradiated orthopaedic material possesses a gel content of between about 95% to about 99%.
5. The method of claim 1 , wherein the irradiated orthopaedic material possesses a degree of swelling of between about 1.7 to about 3.6, and a molecular weight between crosslinks of between about 400 to about 3,500 g/mol.
6. The method of claim 1 , wherein the irradiated orthopaedic material possesses a molecular weight between crosslinks of between about 400 to about 3500 g/mol, and a gel content of between 95% to about 99%.
7. The method of claim 1 , wherein the irradiated orthopaedic material possesses a degree of swelling of between about 1.7 to about 3.6, and a gel content of between 95% to about 99%.
8. The method of claim 1 , wherein the irradiated orthopaedic material possesses a degree of swelling of between about 1.7 to about 3.6, a molecular weight between crosslinks of between about 400 to about 3,500 g/mol, and a gel content of between 95% to about 99%.
9. The method of claim 1 , wherein the total radiation dose is from above 5 Mrad to about 10 Mrad.
10. The method of claim 1 , wherein the polyethylene is ultra-high molecular weight polyethylene or high molecular weight polyethylene.
11. The method of claim 1 , wherein the irradiating uses gamma radiation or electron beam radiation.
12. The method of claim 1 wherein the total radiation dose is delivered in time-separated stages.
13. The method of claim 12 wherein a portion of the total radiation dose is delivered before the orthopaedic material is packaged and another portion of the total radiation dose is delivered after the orthopaedic material is packaged.
14. The method of claim 1 wherein all of the radiation dose is delivered after the orthopaedic material is packaged.
15. The method of claim 1 wherein all of the radiation dose is delivered before the orthopaedic material is formed into an implant.