Tank for electrical equipment
View Patent ↗A tank for electrical equipment such as power transformers and shunt reactors has integral stiffeners for reinforcing the tank during overpressure conditions, such as during an arc fault. The stiffeners are formed of a material that is more ductile than the material to which the stiffeners are attached, such as the tank walls and cover. The tank with integral stiffeners allows for expansion of the internal volume of the tank during overpressure conditions, thus, increasing the flexibility of the tank and mitigating the risk of tank rupture.
1. A tank for a power transformer in an insulating medium, comprising:
a cover, bottom and side walls defining an internal space for receiving the power transformer, said side walls including at least one stiffener joined at predetermined positions to corresponding outer surfaces of said side walls, said at least one stiffener formed of an austenitic stainless steel or mild steel material that has a yield stress value that is lower than or equal to the yield stress value of the material used to form the side walls, said at least one stiffener absorbing arc energy from the insulating medium, wherein said at least one stiffener is formed of an austenitic stainless steel having a chemical composition comprising by weight:
0.03%≦carbon≦0.08%;
0%≦manganese≦2.0%;
0%≦phosphorous≦0.045%;
0%≦sulfur≦0.03%;
0%≦silicon≦0.75%;
8%≦nickel≦14%;
16%≦chromium≦20%;
0%≦molybdenum≦3%;
0%≦nitrogen≦0.1%; and
the remainder being constituted by iron.
2. The tank of claim 1 wherein said stiffeners are joined to said side walls and positioned perpendicularly with respect to a plane of said bottom wall.
3. The tank of claim 1 wherein said stiffeners are joined to said cover and positioned horizontally with respect to a plane of said bottom wall.
4. The tank of claim 1 wherein said cover has said at least one stiffener welded thereto.
5. The tank of claim 1 wherein the stiffener material yield stress value is at least 20 MPa less than the yield stress value of the material used to form said side walls.
6. The tank of claim 1 wherein said stiffener material has an elongation % at break value that is at least ten percent higher than the material used to form said side walls.
7. The tank of claim 4 wherein said at least one stiffener welded to said cover includes a plurality of stiffeners arranged in a grid pattern said stiffeners for reinforcing the connection between said cover and an active part of said transformer.
8. The tank of claim 1 wherein a bushing extends from said cover.
9. A tank for electrical equipment, comprising:
a bottom wall, side walls, and a cover, said cover joined to said side walls; and
a plurality of stiffeners attached at predetermined positions to corresponding outer surfaces of said side walls, said stiffeners formed from an austenitic stainless steel or mild steel material having a measured yield stress value that is lower than or equal to the measured yield stress value of the material used to form the side walls, wherein said stiffeners are formed of an austenitic stainless steel having a chemical composition comprising by weight:
0.03%≦carbon≦0.08%;
0%≦manganese≦2.0%;
0%≦phosphorous≦0.045%;
0%≦sulfur≦0.03%;
0%≦silicon≦0.75%;
8%≦nickel≦14%;
16%≦chromium≦20%;
0%≦molybdenum≦3%;
0%≦nitrogen≦0.1%; and
the remainder being constituted by iron.
10. The tank of claim 9 wherein said stiffeners are joined to said side walls and positioned perpendicularly with respect to a plane of said bottom wall.
11. The tank of claim 9 wherein said stiffeners are joined to said cover and positioned horizontally with respect to a plane of said bottom wall.
12. The tank of claim 10 wherein the stiffener material yield stress value is at least 20 MPa less than the yield stress value of the material used to form said side walls.
13. The tank of claim 9 wherein said cover has at least one of said stiffeners welded thereto.
14. The tank of claim 9 wherein said stiffener material has an elongation % at break value that is at least ten percent higher than the material used to form said side walls.
15. The tank of claim 9 wherein said stiffeners are formed of an austenitic stainless steel additionally comprising, in weight percent: 2%≦molybdenum≦3%.
16. The tank of claim 9 wherein said walls of said tank are formed of a mild steel having a chemical composition comprising by weight:
0%≦carbon≦0.29%;
0.5%≦manganese≦1.5%;
0%≦phosphorous≦0.04%;
0%≦sulfur≦0.05%;
0%≦silicon≦0.4%;
a member selected from the group consisting of: 0%≦niobium+vanadium≦0.1% and at least 0.2% percent by weight copper; and
the remainder being constituted by iron.