Method for producing resin foam, and resin foam

1. A method for producing non-crosslinked resin foam,

the method comprising:

melting a resin composition including 100 parts by weight of a thermoplastic polyolefin resin other than an elastomer wherein the thermoplastic polyolefin resin includes a high melt tension random polypropylene having a first melt tension of 5 cN to 50 cN at 200° C., 35 parts by weight to 55 parts by weight of an amorphous thermoplastic elastomer, and a crystalline elastomer having a higher degree of crystallization than the amorphous thermoplastic elastomer,

wherein the crystalline elastomer is a block copolymer of an linear low-density polyethylene and an ethylene-α-olefin copolymer other than an linear low-density polyethylene, and having a crystallization temperature of 90° C. or higher, wherein the amorphous thermoplastic elastomer is an ethylene-propylene rubber or an ethylene-α-olefin copolymer; impregnating the resin composition with a material, wherein the material is in supercritical state;

foaming the resin composition impregnated with the material by arranging the resin composition under a condition in which the supercritical state of the material is not maintained; and

hot-pressing the foamed resin composition.

2. The method for producing non-crosslinked resin foam according to claim 1 , wherein the foaming is foaming the resin composition while molding the resin composition into a form of a sheet.

3. The method for producing non-crosslinked resin foam according to claim 1 , wherein the thermoplastic polyolefin resin further includes a second polypropylene having a second melt tension at 200° C., wherein the first melt tension is greater than the second melt tension.

4. The method for producing non-crosslinked resin foam according to claim 1 , wherein the resin composition includes 25 parts by weight to 75 parts by weight of the crystalline elastomer.

5. The method for producing non-crosslinked resin foam according to claim 1 , wherein the foaming is extruding the resin composition impregnated with the material that is arranged in an extruding machine under a condition in which the supercritical state of the material is maintained, from the extruding machine through a mouthpiece.

6. The method for producing non-crosslinked resin foam according to claim 1 , wherein a number of cells in a 100 μm square in a cross-section perpendicular to a machine direction of the resin foam is 20 or more.

7. The method for producing non-crosslinked foam resin according to claim 1 , wherein the hot-pressing is hot-pressing the resin composition by supplying the resin composition between a first roller and a second roller, while rotating the first roller and the second roller arranged along the first roller so that a distance from the first roller is shorter than a thickness of the resin composition.

8. A non-crosslinked resin foam having closed-cells, comprising a resin composition comprising:

100 parts by weight of a thermoplastic polyolefin resin other than an elastomer;

35 parts by weight to 55 parts by weight of an amorphous thermoplastic elastomer; and

a crystalline elastomer having a degree of crystallization higher than that of the amorphous thermoplastic elastomer,

wherein the thermoplastic polyolefin resin includes a high melt tension random polypropylene having a first melt tension of 5 cN to 50 cN at 200° C.,

wherein the crystalline elastomer is a block copolymer of an linear low-density polyethylene and an ethylene-α-olefin copolymer other than an linear low-density polyethylene, and having a crystallization temperature of 90° C. or higher,

wherein the amorphous thermoplastic elastomer is an ethylene-propylene rubber or an ethylene-α-olefin copolymer, and

wherein the non-crosslinked resin foam is formed by extrusion foaming while impregnating with a material that is a gas at normal temperature and normal pressure by arranging the resin composition under a condition in which the supercritical state of the material is not maintained.

9. The non-crosslinked resin foam according to claim 8 , wherein

an amount of the crystalline elastomer is 25 parts by weight to 75 parts by weight.

10. The non-crosslinked resin foam according to claim 8 , wherein

a number of cells in a 100 μm square in a cross-section perpendicular to a machine direction is 35 or more.

11. The method for producing non-crosslinked resin foam according to claim 7 , wherein the first roller and the second roller are heated.

12. The non-crosslinked resin foam according to claim 8 , wherein the non-crosslinked resin foam does not comprise a chemical foaming agent.

13. A method for producing the non-crosslinked resin foam according to claim 8 ,

the method comprising:

melting the resin composition including the thermoplastic polyolefin resin other than an elastomer the crystalline elastomer having a higher degree of crystallization than the amorphous thermoplastic elastomer and the amorphous thermoplastic elastomer; impregnating the resin composition with a material, wherein the material is in the supercritical state;

foaming the resin composition impregnated with the material that is a gas at normal temperature and normal pressure by arranging the resin composition under a condition in which the supercritical state of the material is not maintained; and

hot-pressing the foamed resin composition.

14. The method for producing non-crosslinked resin foam according to claim 13 , wherein the material is an inert gas.

15. The method for producing non-crosslinked resin foam according to claim 13 , wherein the material is carbon dioxide.

16. The method for producing non-crosslinked resin foam according to claim 13 , wherein the method is performed without a chemical foaming agent.

17. The non-crosslinked resin foam according to claim 8 , wherein

the thermoplastic polyolefin resin further includes a second polypropylene having a second melt tension at 200° C., the first melt tension being greater than the second melt tension.

18. A non-crosslinked resin foam having closed-cells, comprising:

a thermoplastic polyolefin resin other than an elastomer;

a thermoplastic elastomer; and

a crystalline elastomer having a degree of crystallization higher than that of the thermoplastic elastomer,

wherein the thermoplastic polyolefin resin includes a high melt tension random polypropylene; and

wherein the crystalline elastomer is a block copolymer of an ethylene-α-olefin copolymer and an linear low-density polyethylene, the ethylene-α-olefin copolymer not being an linear low-density polyethylene.

19. The non-crosslinked resin foam according to claim 18 , wherein

the crystalline elastomer includes a plurality of first blocks of the ethylene-α-olefin copolymer and a plurality of second blocks of the linear low-density polyethylene,

each of the first blocks are bounded to at least two of the second blocks,

each of the second blocks includes one end that is bounded to one of the first blocks and another end that is bounded to another block of the first blocks.

20. The non-crosslinked resin foam according to claim 18 , wherein the ethylene-α-olefin copolymer is ethylene-1-octene copolymer.