Paper substrate having enhanced print density
The present invention relates to a sizing composition that, when applied to paper substrate, creates a substrate, preferably suitable for inkjet printing, having increased print density, print sharpness, low HST, and/or image dry time, the substrate preferably having high brightness and reduced color-to-color bleed as well. In addition, the present invention relates to a method of reducing the HST of a paper substrate by applying the sizing composition to at least one surface thereof. Further, the application relates to methods of making and using the sizing composition, as well as methods of making and using the paper containing the sizing composition.
1. A sizing composition, comprising at least one pigment; at least one binder; at least one nitrogen containing organic species; and at least one cationic optical brightening agent, wherein the at least one cationic optical brightening agent is present in an amount from 20 to 40 wt % based on the total weight of the solids in the sizing composition; and at least one inorganic salt, wherein said at least one inorganic salt comprises a halogen counterion.
2. The sizing composition according to claim 1 , comprising at least two binders.
3. The sizing composition according to claim 2 , wherein the at least two binders are polyvinyl alcohol and starch.
4. The sizing composition according to claim 3 , wherein the polyvinyl alcohol and starch are present at a starch/polyvinyl alcohol weight ratio of from 10/1 to 1/5.
5. The sizing composition according to claim 4 , wherein the total binder is present at an amount of at least 20 wt %, based upon the total weight of the solids in the composition.
6. The sizing composition according to claim 2 , wherein the at least one pigment is present in an amount of at least 30 wt % based upon the total weight of the solids in the composition; the total amount of the at least two binders is at least 20 wt % based upon the total weight of the solids in the composition; the at least one nitrogen containing organic species is present in an amount ranging from 1 to 20 wt % based upon the total weight of the solids in the composition; and the at least one inorganic salt is present in an amount ranging from 0.5 to 5 wt % based upon the total weight of the solids in of the composition.
7. The sizing composition according to claim 6 , wherein the at least two binders are starch and polyvinyl alcohol at a weight ratio of from 8/1 to 1/1 starch/polyvinyl alcohol.
8. A paper substrate, comprising the sizing composition according to claim 1 .
9. The paper substrate according to claim 8 , wherein the substrate has a print density of at least 1.0.
10. The paper substrate according to claim 8 , wherein the substrate has a waterfastness of at least 95%.
11. The paper substrate according to claim 8 , wherein the substrate has an HST of not more than 10 seconds.