Carbon nanotubes and methods of forming same at low temperature

1. A method for growth of carbon nanotubes, comprising:

(a) preparing graphene-contained powders; and

(b) heating the graphene-contained powders at a target temperature to form the carbon nanotubes,

wherein the graphene-contained powders comprise graphene sheets decorated with iron oxide nanoparticles, and wherein the target temperature is in a range of about 150° C.-400° C.

2. The method of claim 1 , wherein the graphene sheets comprise multi-layered graphene sheets.

3. The method of claim 1 , wherein the step of preparing the graphene-contained powders comprises:

(a) preparing the graphene sheets having an average dimension of several microns;

(b) treating the graphene sheets with a first solution having carboxylic groups to form a second solution;

(c) filtering, washing and drying the second solution to form a functionalized grapheme powders;

(d) dispersing the functionalized graphene powders in water homogenously to form a third solution;

(e) adding carboxylated iron oxide nanoparticles with the third solution to form a fourth solution; and

filtering and drying the fourth solution to form the iron oxide-graphene powders.

4. The method of claim 3 , wherein the first solution comprises sulfuric and nitric acid.

5. The method of claim 4 , wherein a ratio of the sulfuric and nitric acid is about 3:1.

6. The method of claim 3 , wherein the step of treating the graphene sheets with the first solution having the carboxylic groups to form the second solution further comprises stirring the graphene sheets in the first solution.

7. The method of claim 3 , wherein the step of dispersing the functionalized graphene powders in water homogenously to form the third solution is performed by adding the functionalized graphene powders in a deionized water such that the concentration of graphene in the deionized water is about 1 mg/ml.

8. The method of claim 3 , wherein the carboxylated metal or metal oxide nanoparticles have a diameter in a range of about 5-15 nm.

9. The method of claim 3 , wherein the iron oxide nanoparticles and the third solution are mixed in a 1:1 ratio through sonication.

10. The method of claim 3 , wherein the fourth solution is dried at a temperature in a range of about 50-150° C.

11. The method of claim 10 , wherein the fourth solution is dried at a temperature of about 100° C.

12. The method of claim 1 , wherein the step of heating the graphene-contained powders to form the carbon nanotubes is performed in an electrical furnace.

13. The method of claim 1 , wherein the step of heating the graphene-contained powders to form the carbon nanotubes is performed in a radio-frequency (RF) generator with a frequency.

14. The method of claim 13 , wherein the frequency is in a range of about 100-700 kHz.

15. The method of claim 13 , wherein the step of heating the graphene-contained powders to form the carbon nanotubes is performed in an argon/hydrogen environment that is devoid of a hydrocarbon source.

16. The method of claim 15 , wherein the step of heating the graphene-contained powders to form the carbon nanotubes comprises:

(a) spreading the iron oxide-graphene powders on a graphite boat placed inside a quartz tube that is positioned at a center of a generator coil of the RF generator;

(b) flushing the iron oxide-graphene powders with argon;

(c) turning on the RF generator;

(d) heating the iron oxide-graphene powders to the target temperature;

(e) adding hydrogen in the graphite boat at a desired rate for a predetermined time;

(f) turning off the RF generator and stopping adding the hydrogen; and

(g) cooling it to the room temperature under an argon flow.

17. A method for growth of carbon nanotubes, comprising:

(a) providing a graphitic composite;

(b) decorating the graphitic composite with iron oxide nanostructures to form graphene-contained powders; and

(c) heating the graphene-contained powders at a target temperature to form the carbon nanotubes in an argon/hydrogen environment that is devoid of a hydrocarbon source, wherein the target temperature is in a range of about 150° C.-400° C.

18. The method of claim 17 , wherein the graphitic composite comprises graphene sheets, multi-layered graphenes, graphite fullerenes, nanofibers, or nanowires.

19. The method of claim 17 , wherein the iron oxide nanoparticles have a diameter in a range of about 5-15 nm.

20. The method of claim 17 , wherein the step of heating the graphene-contained powders to form the carbon nanotubes is performed in an electrical furnace.

21. The method of claim 17 , wherein the step of heating the graphene-contained powders to form the carbon nanotubes is performed in a radio-frequency (RF) generator.