Gypsum composites used in fire resistant building components
A composite product includes gypsum in an amount of 60 to 90% by weight, fibers in an amount of 1.5 to 26% by weight substantially homogeneously distributed through the composite, and a rheology-modifying agent in an amount of 0.5 to 6% by weight. The composite is caused or allowed to cure to form a cured composite. The cured composite is a fire resistant component used in a fire-rated door core, a fire-rated door or a fire-rated building panel. The fire resistant component may include a building panel, a door panel, a door core, a door rail, a door stile, a door lock block, a door border, or a door insert.
1. A fire resistant composite product comprising:
a composite comprising gypsum in an amount sufficient to provide fire resistance wherein the amount is 60 to 90% by weight, fibers in an amount of 1.5 to 26% by weight substantially homogeneously distributed through the composite, and a rheology-modifying agent in an amount of 0.5 to 6% by weight;
wherein the fibers comprise glass fibers, cellulose fibers, polyvinyl alcohol fibers and polypropylene fibers;
wherein the rheology-modifying agent comprises hydroxypropoyl methyl celluose (HPMC), methyl hydroxyethyl cellulose (MHEC), hydroxyethyl cellulose (HEC) or carboxymethyl cellulose (CMC);
the composite is caused or allowed to cure to form a cured composite; and
the cured composite is a fire resistant component used in a fire-rated door core, a fire-rated door or a fire-rated building panel, wherein the fire resistant component is selected from a building panel, a door panel, a door core, a door rail, a door stile, a door lock block, a door border, and a door insert.
2. The fire resistant composite product as recited in claim 1 , wherein the composite further comprises an aggregate in an amount of 10 to 25% by weight substantially homogeneously distributed through the composite.
3. The fire resistant composite product as recited in claim 1 , wherein the composite further comprises a starch in an amount of 2 to 7% by weight.
4. The fire resistant composite product as recited in claim 1 , wherein the composite further comprises a vermiculite or clay in an amount of 1 to 10% by weight substantially homogeneously distributed through the composite.
5. The fire resistant composite product as recited in claim 1 , wherein the composite does not include any cement or flyash.
6. The fire resistant composite product as recited in claim 1 , wherein the glass fibers are in an amount of 1.5 to 5% by weight.
7. The fire resistant composite product as recited in claim 1 , wherein:
the glass fibers are in an amount of 2 to 10% by weight;
the cellulose fibers are in an amount of 2 to 8% by weight;
the polyvinyl alcohol fibers are in an amount of 1 to 4% by weight; and
the polypropylene fibers are in an amount of 0.3 to 4% by weight.
8. A fire resistant composite product comprising:
a composite consisting of gypsum in an amount sufficient to provide fire resistance wherein the amount is 60 to 85% by weight, fibers in an amount of 1.5 to 5% by weight substantially homogeneously distributed through the composite, an aggregate in an amount of 10 to 25% by weight substantially homogeneously distributed through the composite, a starch in an amount of 2 to 7% by weight and a rheology-modifying agent in an amount of 0.5 to 4% by weight;
the composite is caused or allowed to cure to form a cured composite; and
the cured composite is a fire resistant component used in a fire-rated door core, a fire-rated door or a fire-rated building panel, wherein the fire resistant component is selected from a building panel, a door panel, a door core, a door rail, a door stile, a door lock block, a door border, and a door insert.
9. The fire resistant composite product as recited in claim 8 , wherein the composite further comprises a vermiculite or clay in an amount of 1 to 10% by weight substantially homogeneously distributed through the composite.
10. The fire resistant composite product as recited in claim 8 , wherein the fibers have a diameter of 6 mm to 25 mm.
11. The fire resistant composite product as recited in claim 8 , wherein the rheology-modifying agent comprises hydroxypropoyl methyl celluose (HPMC), methyl hydroxyethyl cellulose (MHEC), hydroxyethyl cellulose (HEC) or carboxymethyl cellulose (CMC).
12. The fire resistant composite product as recited in claim 8 , wherein the aggregate have an average particle diameter of 1 to 4 mm.
13. The fire resistant composite product as recited in claim 8 , wherein the fibers comprise glass fibers, cellulose fibers polyvinyl alcohol fibers, polypropylene fibers, or a combination thereof.
14. The fire resistant composite product as recited in claim 8 , wherein the fire resistant component has a cross-sectional thickness of 0.125 inches to 2 inches, a width of 1 inch to 4 feet and a length of 3 to 10 feet.
15. The fire resistant composite product as recited in claim 8 , wherein the composite does not include any cement or flyash.
16. A fire resistant composite product comprising:
a composite comprising gypsum in an amount sufficient to provide fire resistance wherein the amount is 70 to 90% by weight, glass fibers in an amount of 2 to 10% by weight substantially homogeneously distributed through the composite, cellulose fibers in an amount of 2 to 8% by weight substantially homogeneously distributed through the composite, polyvinyl alcohol fibers in an amount of 1 to 4% by weight substantially homogeneously distributed through the composite, polypropylene fibers in an amount of 0.3 to 4% by weight substantially homogeneously distributed through the composite, and a rheology-modifying agent in an amount of 0.5 to 6% by weight;
wherein the rheology-modifying agent comprises hydroxypropoyl methyl celluose (HPMC), methyl hydroxyethyl cellulose (MHEC), hydroxyethyl cellulose (HEC) or carboxymethyl cellulose (CMC);
the composite is caused or allowed to cure to form a cured composite; and
the cured composite is a fire resistant component used in a fire-rated door core, a fire-rated door or a fire-rated building panel, wherein the fire resistant component is selected from a building panel, a door panel, a door core, a door rail, a door stile, a door lock block, a door border, and a door insert.
17. The fire resistant composite product as recited in claim 16 , wherein the fibers have a diameter of 6 mm to 25 mm.
18. The fire resistant composite product as recited in claim 16 , wherein the fire resistant component has a cross-sectional thickness of 0.125 inches to 2 inches, a width of 1 inch to 4 feet and a length of 3 to 10 feet.
19. The fire resistant composite product as recited in claim 16 , wherein the composite does not include any cement or flyash.