Anti-powdering and anti-static polymer film for digital printing
A coated polymer film, such as a coated polyester film, is disclosed. In one embodiment, the coated film may be used as a substrate for digital printing. In one embodiment, the coating contains an anionic anti-static agent comprising a sulphonated copolyester resin. In an alternative embodiment, the coating contains an anti-static agent comprising an organometallic, such as an organo zirconate, in combination with metal oxide particles. The metal oxide particles may comprise nanoparticles. In one embodiment, the coating can further contain a print enhancing agent and an adhesion promoter.
1. A coated film having anti-static and/or anti-dusting properties comprising:
a base film having a first side and a second side, the base film comprising a colored film containing a pigment in an amount from about 5% by weight to about 30% by weight; and
a coating on at least the first side of the film, the coating comprising:
an anti-static agent comprising an anionic copolyester;
an adhesion promoter comprising an alkylene and acrylic acid copolymer present in the dried coating in an amount of from about 20% to about 55% by weight,
a print enhancing agent comprising a vinyl ether present in the dried coating in an amount of from about 10% to about 35% by weight; and
polymethylmethacrylate particles, wherein the polymethylmethacrylate particles are present in the coating in an amount from about 0.5% to about 3% by weight; and
wherein the coated film is free of conductive materials other than the anionic copolyester.
2. A coated film as defined in claim 1 , wherein the print enhancing agent comprises poly(vinyl methyl ether) or poly(vinyl ethyl ether).
3. A coated film as defined in claim 1 , wherein the anti-static agent is present in the coating in an amount from about 20% to about 40% by weight, the coating further comprising:
a crosslinking agent.
4. A coated film as defined in claim 3 , wherein the print enhancing agent comprises a polyvinyl methyl ether, the print enhancing agent being present in the coating in an amount from about 15% to about 30% by weight; and
wherein the adhesion promoter comprises an ethylene acrylic acid copolymer, the adhesion promoter being present in the coating in an amount from about 30% to about 50% by weight.
5. A coated film as defined in claim 3 , wherein the crosslinking agent comprises a melamine, the crosslinking agent being present in the coating in an amount from about 1% to about 5% by weight.
6. A coated film as defined in claim 1 , wherein the anti-static agent comprises a water-soluble copolyester comprising 1,3-benzenedicarboxylic acid, 5-sulfo-, 1,3-dimethyl ester sodium salt, polymer and dimethyl 1,4-benzenedicarboxylate, 1,2-ethanediol and 2,2′-oxybis(ethanol).
7. A coated film as defined in claim 1 , wherein the coating is also on the second side of the base film.
8. A coated film as defined in claim 1 , wherein the pigment comprises a white pigment and wherein the white pigment comprises titanium dioxide, barium sulfate, magnesium oxide, calcium carbonate, or mixtures thereof, the white pigment having an average particle size of from about 0.05 microns to about 0.5 microns.
9. A coated film as defined in claim 1 , wherein the base film comprises a polyester film, that has been biaxially stretched.
10. A coated film as defined in claim 1 , wherein the coating has a thickness of from about 130 nm to about 200 nm.
11. A coated film as defined in claim 1 , wherein the film further includes printed matter applied to the coating on the first side of the film, the printed matter comprising a toner.
12. A coated film as defined in claim 11 , wherein the toner comprises digital printer toner.
13. A coated film as defined in claim 1 , wherein the anti-static agent comprises a sulphonated copolyester.
14. A coated film as defined in claim 13 , wherein the anti-static agent is present in the coating in an amount from about 10% by weight to about 60% by weight.
15. A coated film as defined in claim 1 , wherein the base film is a colored and matte film.
16. A coated film as defined in claim 1 , wherein the alkylene and acrylic acid copolymer contains the acrylic acid monomer in an amount from about 8% to about 18% by weight.
17. A coated film having anti-static and/or anti-dusting properties comprising:
a base film having a first side and a second side, the base film comprising a colored film containing a pigment in an amount from about 5% by weight to about 30% by weight; and
a coating on at least the first side of the film, the coating comprising:
an anti-static agent comprising an anionic copolyester;
an adhesion promoter comprising an alkylene and acrylic acid copolymer present in the dried coating in an amount of from about 20% to about 55% by weight;
a print enhancing agent comprising a vinyl ether present in the coating in an amount from about 10% to about 35% by weight;
a crosslinking agent in an amount of about 1% to about 5% by weight; and
polymethylmethacrylate particles, wherein the polymethylmethacrylate particles are present in the coating in an amount from about 0.5% to about 3% by weight; and
wherein the coated film is free of conductive materials other than the anionic copolyester.
18. A coated film as defined in claim 17 , wherein the anti-static agent is present in the coating in an amount from about 20% to about 40% by weight.