Composite knife
A composite knife made from layers of Metal Matrix Composite (MMC) is disclosed. It includes a middle layer of fibrous preform including a hard insert placed longitudinally at its periphery. The hard insert, after sharpening, represents the cutting blade portion of the composite knife. The composite knife further includes a carrier which forms the load bearing member of the cutting blade, as well as forming the integral handle of the composite knife. The carrier portion of the composite knife includes at least one top and at least one bottom layers of fibrous preform, sandwiching the middle layer that contains the cutting edge portion of the knife. A metallic material is infiltrated within the fibrous preforms and extends throughout the composite blade structure forming the MMC knife, the metallic material bonding the middle layer within the carrier, and bonding the top and bottom surface of the hard insert within the carrier.
1. A composite knife, comprising:
a middle layer of fibrous preform, a portion of said middle layer comprising a ceramic insert placed longitudinally at the periphery of said middle layer and being substantially coplanar with said fibrous preform, said ceramic insert including a top surface and a bottom surface, and an exposed cutting blade portion;
a carrier structure to support said exposed cutting blade portion, said carrier structure comprising at least one top layer and at least one bottom layer of fibrous preform, said middle layer disposed between said at least one top layer and said at least one bottom layer and in contact thereto;
a metallic material, said metallic material infiltrated within said middle layer said metallic material bonding said middle layer within said carrier structure, said metallic material bonding said top and bottom surfaces of said ceramic insert to said carrier structure, said metallic material extending outward to encapsulate said composite knife; and
wherein said composite knife has a density of <4.7 gr/cc.
2. A composite knife as in claim 1 wherein said middle layer of fibrous preform comprises discontinuous ceramic fibers having between 3 and 30 percent fiber content.
3. A composite knife as in claim 1 wherein said top and bottom layers of the fibrous preform each comprises continuous ceramic fibers having between 20 percent and 70 percent fiber content.
4. A composite knife as in claim 1 wherein said top, bottom, and middle layers are symmetrical.
5. A composite knife as in claim 1 , wherein said ceramic insert includes a plurality of holes placed away from said exposed cutting blade portion, and wherein said metallic material bonds within said holes and outward to said fibrous preforms of said carrier structure.
6. A composite knife as in claim 1 wherein said at least one top layer and said at least one bottom layer each has a thickness of at least equal to the thickness of said middle layer.
7. A composite knife as in claim 1 wherein said middle layer has a thickness of at least 1 mm.
8. A composite knife as in claim 1 , wherein said metallic material is selected from the group consisting of aluminum alloys, and magnesium.
9. A composite knife as in claim 1 , wherein the ceramic insert is tungsten carbide.
10. A composite knife as in claim 1 , wherein the ceramic insert is selected from the group consisting of ceramics, metals, carbon/graphite materials, or composites with dense microstructures.
11. A composite knife as in claim 3 , wherein said continuous ceramic fibers are Nextel Ceramic Oxide fiber 610.
12. A composite knife as in claim 2 , wherein said discontinuous ceramic fibers are selected from the group consisting of alumina, alumina-silica, SiC or Bn.
13. A composite knife, comprising:
a middle layer of fibrous preform, a portion of said middle layer comprising a ceramic insert placed longitudinally at the periphery of said middle layer and being substantially coplanar with said fibrous preform, said ceramic insert including a top surface and a bottom surface, and an exposed cutting blade portion;
a carrier structure to support said exposed cutting blade portion, said carrier structure comprising at least one top layer and at least one bottom layer of fibrous preform, said middle layer disposed between said at least one top layer and said at least one bottom layer and in contact thereto;
a metallic material, said metallic material infiltrated within said middle layer said metallic material bonding said middle layer within said carrier structure, said metallic material bonding said top and bottom surfaces of said ceramic insert to said carrier structure, said metallic material extending outward to encapsulate said composite knife and
wherein said composite knife has a density of <4.7 gr/cc; and
wherein said middle layer of fibrous preform comprises discontinuous ceramic fibers having between 3 and 30 percent fiber content; and
wherein said top and bottom layers of said fibrous preform each comprises continuous ceramic fibers having between 20 percent and 70 percent fiber content.
14. A composite knife, comprising:
a middle layer of fibrous preform, a portion of said middle layer comprising a ceramic insert placed longitudinally at the periphery of said middle layer and being substantially coplanar with said fibrous preform, said ceramic insert including a top surface and a bottom surface, and an exposed cutting blade portion;
a carrier structure to support said exposed cutting blade portion, said carrier structure comprising at least one top layer and at least one bottom layer of fibrous preform, said middle layer disposed between said at least one top layer and said at least one bottom layer and in contact thereto;
a metallic material, said metallic material infiltrated within said middle layer said metallic material bonding said middle layer within said carrier structure, said metallic material bonding said top and bottom surfaces of said ceramic insert to said carrier structure, said metallic material extending outward to encapsulate said composite knife.
15. A composite knife as in claim 14 , wherein said composite knife has a density of <4.7 gr/cc.
16. A composite knife as in claim 14 , wherein said middle layer of fibrous preform comprises discontinuous ceramic fibers having between 3 and 30 percent fiber content.
17. A composite knife as in claim 14 , wherein said top and bottom layers of said fibrous preform each comprises continuous ceramic fibers having between 20 percent and 70 percent fiber content.
18. A composite knife as in claim 14 , wherein said ceramic insert includes a plurality of holes placed away from said exposed cutting blade portion, and wherein said metallic material bonds within said holes and outward to said fibrous preforms of said carrier structure.
19. A composite knife as in claim 14 wherein said at least one top layer and said at least one bottom layer each has a thickness of at least equal to the thickness of said middle layer.
20. A composite knife as in claim 14 wherein said middle layer has a thickness of at least 1 mm.