Hot melt adhesive
A hot melt adhesive material and articles made using the hot melt adhesive to assemble structures in an article. The adhesive material typically is manufactured by blending amorphous polymer with a compatible amorphous polymer.
1. A hot melt adhesive composition comprising:
(i) from about 50 wt. % to about 90 wt. % of an amorphous polyolefin copolymer comprising more than 40 mole % 1-butene, the amorphous polyolefin copolymer having a viscosity of between 2000 and 8000 cps at a temperature of about 190° C.; and
(ii) from about 10 wt. % to about 50 wt. % of a second amorphous polymer comprising at least one butene monomer, the second amorphous polymer having a molecular weight (MW n ) of at least 1000, wherein the second amorphous polymer is compatible with the amorphous polyolefin copolymer.
2. The hot melt adhesive composition of claim 1 , wherein the adhesive is substantially free of a tackifier.
3. The hot melt adhesive composition of claim 1 , wherein the second amorphous polymer comprises a viscous liquid with molecular weight of about 1,000-20,000 and a Saybolt Universal seconds (SUS) viscosity at 100° C. of about 100 to 20,000.
4. The hot melt adhesive composition of claim 1 , wherein the second amorphous polymer comprises a polyisobutylene with a molecular weight of 1,500 to 6,000.
5. The hot melt adhesive composition of claim 1 , wherein the density of the adhesive composition is less than 0.9 g-cm −3 .
6. The hot melt adhesive composition of claim 1 , wherein the density of the adhesive composition is less than 0.87 g-cm −3 .
7. A disposable article comprising a substrate combined with a film, fiber, cellulose sheet or non-woven having an adhesive bond there between comprising the adhesive of claim 1 .
8. A disposable diaper article comprising a substrate combined with a film, fiber, cellulose sheet or non-woven having an adhesive bond there between comprising the adhesive of claim 1 .
9. The hot melt adhesive composition of claim 1 , wherein the adhesive is substantially free of a tackifier.
10. The hot melt adhesive composition of claim 1 , wherein the second amorphous polymer comprises a viscous liquid with molecular weight of about 1,000-20,000 and a Saybolt Universal seconds (SUS) viscosity at 100° C. of about 100 to 20,000.
11. The hot melt adhesive composition of claim 1 , wherein the second amorphous polymer comprises a polyisobutylene with a molecular weight of 1,500 to 6,000.
12. The hot melt adhesive composition of claim 1 , wherein the density of the adhesive is less than 0.9 g-cm −3 .
13. The hot melt adhesive composition of claim 1 , wherein the density of the adhesive is less than 0.87 g-cm −3 .
14. A hot melt adhesive composition comprising:
(i) about 90 wt. % to about 10 wt. % of an amorphous polyolefin composition comprising a copolymer having more than 40 mole % 1-butene, the copolymer having a viscosity of between 2000 and 8000 cps at a temperature of 190° C.; and
(ii) about 0.1 wt. % to about 50 wt. % of a polyisobutylene;
wherein the adhesive composition is substantially free of a tackifier;
wherein the hot melt adhesive composition has a softening point temperature range of 115° C. to about 130° C.
15. The hot melt adhesive composition of claim 14 , wherein the polyisobutylene has a molecular weight of about 2000 to 3000.
16. The hot melt adhesive composition of claim 14 , wherein the density of the adhesive composition is less than 0.9 g-cm −3 .
17. The hot melt adhesive composition of claim 14 , wherein the density of the adhesive composition is less than 0.87 g-cm −3 .
18. A disposable article comprising a substrate combined with a film, fiber, cellulose sheet or non-woven having an adhesive bond there between comprising the adhesive of claim 14 .
19. A disposable diaper article comprising a substrate combined with a film, fiber, cellulose sheet or non-woven having an adhesive bond there between comprising the adhesive of claim 14 .
20. A hot melt adhesive composition consisting essentially of:
(i) a blend of amorphous polyolefin copolymers, each amorphous polyolefin copolymer comprising more than 40 mole % 1-butene, at least one amorphous polyolefin copolymer having a viscosity of between 2000 and 8000 cps at a temperature of 190° C.; and
(ii) a second amorphous polymer comprising at least one butene monomer, the polymer having a molecular weight (MW) of at least 1000 wherein the polymer is compatible with the polyolefin.
21. A disposable article comprising a substrate combined with a film, fiber, cellulose sheet or non-woven having an adhesive bond there between comprising the adhesive of claim 20 .
22. A disposable diaper article comprising a substrate combined with a film, fiber, cellulose sheet or non-woven having an adhesive bond there between comprising the adhesive of claim 20 .
23. A hot melt adhesive composition consisting essentially of:
(i) an amorphous polyolefin copolymer comprising more than 40 mole % 1-butene, the amorphous polyolefin copolymer having a viscosity of between 2000 and 8000 cps at a temperature of 190° C.; and
(ii) a second amorphous polymer comprising at least one butene monomer, the second amorphous polymer having a molecular weight (MW n ) range of about 5,000 to about 45,000, wherein the second amorphous polymer is compatible with the amorphous polyolefin copolymer;
wherein the hot melt adhesive composition has a softening point temperature range of 115° C. to about 130°.