Removal of surface passivation
Methods for removing a passivation film from a copper surface can include exposing the passivation film to a vapor phase organic reactant, for example at a temperature of 100° C. to 400° C. In some embodiments, the passivation film may have been formed by exposure of the copper surface to benzotriazole, such as can occur during a chemical mechanical planarization process. The methods can be performed as part of a process for integrated circuit fabrication. A second material can be selectively deposited on the cleaned copper surface relative to another surface of the substrate.
1. A method for removing a passivation film from a substrate, the method comprising:
providing the substrate comprising a passivation film on a metal surface, wherein the passivation film was formed by exposure of the metal surface to a passivation agent comprising a hydrocarbon; and
exposing the passivation film to a vapor phase organic reactant at a temperature of 100° C. to 400° C., wherein the passivation film is not exposed to a plasma during exposure of the passivation film to the vapor phase organic reactant.
2. The method of claim 1 , wherein the vapor phase organic reactant comprises carboxylic acid.
3. The method of claim 1 , wherein the vapor phase organic reactant comprises formic acid.
4. The method of claim 1 , wherein the passivation agent comprises an aromatic hydrocarbon.
5. The method of claim 1 , wherein the passivation agent comprises benzotriazole.
6. The method of claim 1 , further comprising repeating exposing the passivation film to the vapor phase organic reactant at least 10 times.
7. The method of claim 1 , wherein the metal surface is a copper surface.
8. The method of claim 1 , wherein the substrate further comprises a dielectric material, and wherein a surface chemistry of the dielectric material is substantially unaffected by exposing the passivation film to the vapor phase organic reactant.
9. A method for integrated circuit fabrication, comprising:
providing a substrate comprising a passivation film on a copper surface that was subjected to a chemical mechanical planarization process;
performing a cleaning process for removing the passivation film from the copper surface, wherein performing the cleaning process comprises:
contacting the passivation film with a vapor phase organic reactant at a process temperature of 100° C. to 400° C.,
wherein the vapor phase organic reactant has the formula R—COOH, the R being a hydrogen, or a C 1 -C 3 alkyl, and
wherein the cleaning process is substantially free of plasma activated reactants.
10. The method of claim 9 , wherein during the chemical mechanical planarization process the copper surface was exposed to benzotriazole.
11. The method of claim 9 , wherein the vapor phase organic reactant comprises formic acid.
12. The method of claim 9 , wherein the substrate further comprises a dielectric material, and wherein a surface chemistry of the dielectric material is substantially unaffected by the cleaning process.
13. The method of claim 9 , wherein the process temperature is 200° C. to 250° C.
14. A method of integrated circuit fabrication, comprising:
cleaning a copper surface of a substrate by removing a passivation film that was formed on the copper surface by exposure to a hydrocarbon passivation agent,
wherein cleaning comprises contacting the passivation film with a vapor phase organic reactant substantially without exposing the substrate to a plasma; and
selectively depositing a second material on the cleaned copper surface relative to a second surface on the substrate.
15. The method of claim 14 , wherein the passivation agent comprises benzotriazole and the vapor phase organic reactant comprises a carboxylic acid.
16. The method of claim 14 , wherein the passivation film comprises a coordination complex formed by the copper and the passivation agent.
17. The method of claim 14 , wherein the passivation film is removed at a process temperature of 100° C. to 400° C.
18. The method of claim 14 , wherein the second material comprises an electrically conductive material.
19. The method of claim 18 , wherein the second material comprises tungsten.
20. The method of claim 14 , wherein the second material comprises an electrically insulating material.
21. The method of claim 14 , wherein the second surface comprises a dielectric material, and wherein the second material is substantially not deposited on the dielectric material.