RARE EARTH-COBALT PERMANENT MAGNET
There is provided a rare earth-cobalt permanent magnet containing 23 to 27 wt % R, 3.5 to 5 wt % Cu, 19 to 25 wt % Fe, 1.5 to 3 wt % Zr, and a remainder Co with inevitable impurities, where an element R is a rare earth element at least containing Sm. The rare earth-cobalt permanent magnet has a density of 8.15 to 8.39 g/cm 3 . It also has a metal structure including a cell phase ( 11 ) containing Sm 2 Co 17 phase and a cell wall ( 12 ) surrounding the cell phase and containing SmCo 5 phase. An average crystal grain diameter is within a range of 40 to 100 μm. A half width of Cu content of the cell wall ( 12 ) is 10 nm or less.
1 . A rare earth-cobalt permanent magnet containing 23 to 27 wt % R, 3.5 to 5 wt % Cu, 19 to 25 wt % Fe, 1.5 to 3 wt % Zr, and a remainder Co with inevitable impurities, where an element R is a rare earth element at least containing Sm, wherein
the rare earth-cobalt permanent magnet has a density of 8 . 15 to 8 . 39 g/cm 3 ,
the rare earth-cobalt permanent magnet has a metal structure including a cell phase containing Sm 2 Co 17 phase and a cell wall surrounding the cell phase and containing SmCo 5 phase,
an average crystal grain diameter is within a range of 40 to 100 μm, and
a half width of Cu content of the cell wall is 10 nm or less.
2 . The rare earth-cobalt permanent magnet according to claim 1 , wherein a maximum value of Cu content of the cell wall is 15 at % or more.
3 . The rare earth-cobalt permanent magnet according to claim 1 , wherein among the inevitable impurities, C is restricted to 200 to 1000 ppm.
4 . The rare earth-cobalt permanent magnet according to claim 1 , wherein among the inevitable impurities, O is restricted to 1000 to 5000 ppm.