Brazing compositions and uses thereof
Described herein are compositions for use in the brazing of metal substrates, methods of making and using these compositions are also described herein. Heat exchangers often have a distributor tube whose external surface is provided with cooling fins. The distributor tube is typically a steel tube coated with a metal having good heat conduction, such as aluminum. The cooling fins themselves also generally comprise aluminum because of its good heat conductivity and low weight.
1. A brazing composition consisting of a non-aqueous blend of:
a metal halide;
from about 40 wt. % to about 65 wt. % of a hydrophobic carrier; and
propylene glycol in an amount ranging from about 1 wt. % to about 25 wt. % based on the total weight of the brazing composition.
2. The brazing composition of claim 1 , wherein the metal halide is selected from: potassium fluoride; aluminum fluoride; cesium fluoride; rubidium fluoride; lithium fluoride; sodium fluoride; calcium fluoride; potassium aluminum fluoride; cesium aluminum fluoride; lithium aluminum fluoride; and a combination of two or more thereof.
3. The brazing composition of claim 1 , wherein the hydrophobic carrier is a liquid at room temperature.
4. The brazing composition of claim 1 , wherein the composition is acrylate-free.
5. The brazing composition of claim 1 , having a bonding temperature of from about 550° C. to about 650° C.
6. A brazing composition consisting of:
a non-aqueous mixture of: a metal halide; a hydrophobic carrier; and a glycol selected from the group consisting of hexylene glycol, propylene glycol, and combinations thereof; and
a filler metal having greater than 50 wt. of aluminum based on the total weight of the filler metal.
7. The composition of claim 6 , wherein the filler metal has an average particle size that is greater than the average particle size of the metal halide.
8. The brazing composition of claim 6 , wherein the non-aqueous mixture and the filler metal are maintained separately prior to use and the filler metal is a substantially planar substrate.
9. The brazing composition of claim 6 , wherein the metal halide is selected from: potassium fluoride; aluminum fluoride; cesium fluoride; rubidium fluoride; lithium fluoride; sodium fluoride; calcium fluoride; potassium aluminum fluoride; cesium aluminum fluoride; lithium aluminum fluoride; and a combination of two or more thereof.
10. The brazing composition of claim 6 , wherein the filler metal is selected from aluminum, silicon, zinc, an alloy of aluminum and zinc; an alloy of zinc, aluminum and silicon, an alloy of aluminum and silicon; and a combination of two or more thereof.
11. The brazing composition of claim 6 , wherein the filler metal has an average particle size of from about 1 to about 500 microns.
12. The brazing composition of claim 6 , wherein the filler metal has greater than 85 wt. % aluminum based on the total weight of the filler metal.
13. The brazing composition of claim 6 , wherein the hydrophobic carrier is present in an amount of from about 48 wt % to about 58 wt % of the non-aqueous mixture.
14. The brazing composition of claim 6 , wherein the glycol is present in an amount ranging from about 1 wt. % to about 25 wt. % based on the total weight of the first component.
15. The brazing composition of claim 6 , having a bonding temperature of from about 550° C. to about 650° C.
16. The brazing composition of claim 8 , wherein the substantially planar substrate has a thickness of from about 0.010 to about 0.15 inches.
17. The brazing composition of claim 11 , wherein the filler metal has an average particle size of from about 1 to about 25 microns.
18. The brazing composition of claim 17 , wherein the filler metal has an average particle size of from about 1 to about 10 microns.