Compositions for cooling materials exposed to the sun
View Patent ↗The present invention provides for a composition comprising a pigment, wherein the composition is suitable for coating a surface that is, or is expected to be, exposed to the sun. The pigment comprises particles that fluoresce in sunlight, thereby remaining cooler in the sun than coatings pigmented with non-fluorescent particles. The particles comprise solids that fluoresce or glow in the visible or near infrared (NIR) spectra, or that fluoresce when doped. Suitable dopants include, but are not limited to, ions of rare earths and transition metals.
1. A coating composition comprising:
a transparent binder; and
a pigment comprising Al 2 O 3 doped with Cr 2 O 3 ,
wherein the weight percent of Cr 2 O 3 dopant ranges from 0.5 to 4% of the total weight of the pigment.
2. The coating composition of claim 1 , wherein the weight percent of Cr 2 O 3 dopant ranges from 1 to 4% of the total weight of the pigment.
3. The coating composition of claim 1 , wherein the coating composition exhibits a dark color.
4. The coating composition of claim 3 , wherein the dark color is black, red, blue, and/or green.
5. The coating composition of claim 1 , wherein the pigment fluoresces within the 700 to 1,000 nm range.
6. The coating composition of claim 1 , further comprising a metal oxide or metal fluoride, or metal compound doped with one or more rare earth elements or a transition metal.
7. The coating composition of claim 6 , wherein the metal oxide or metal fluoride, or metal compound, is doped with Nd, Pm, Dy, Ho, Er, Tm, Yb, or Cr.
8. The coating composition of claim 6 , wherein the metal oxide is YAlO 3 doped with one or more rare earth elements or a transition metal.
9. The coating composition of claim 8 , wherein the metal oxide is YAlO 3 doped with Nd, Pm, Dy, Ho, Er, Tm, Yb, or Cr.
10. The coating composition of claim 6 , wherein the metal compound is a cadmium compound.
11. The coating composition of claim 10 , wherein the cadmium compound is CdS, CdSe, or CdTe.
12. The coating composition of claim 1 , wherein the coating composition is suitable for application over a surface of a roofing or siding material or an automotive finish.
13. A substrate exposed to or expected to be exposed to the sun coated with a coating composition including the coating composition of claim 1 .
14. The substrate of claim 13 , wherein the substrate is a roofing or siding material or an automotive finish.