Ultra-light ultra-strong proppants
The present invention provides a method of preparing a proppant material by heating a reaction mixture comprising a plurality of oxides in a reactive atmosphere to a temperature above the melting point of the reaction mixture to form a melt, and then allowing the melt to solidify in a mold in the form of spherical particles. The present invention also provides a method of preparing a proppant material by heating a reaction mixture comprising a plurality of oxides and one or more additives in a reactive atmosphere to a temperature below the melting point of the reaction mixture to form a powder including one or more reaction products, and then processing the powder to form spherical particles. The present invention also provides a proppant material including spherical particles characterized by a specific gravity of about 1.0 to 3.0 and a crush strength of at least about 10,000 psi.
1. A method of preparing a proppant material comprising:
heating a reaction mixture comprising a plurality of oxides from a combination of metallurgical slag and flyash, wherein the reaction mixture is in a mold and is heated in a reactive atmosphere to a temperature above the melting point of the reaction mixture to form a melt; and
allowing the melt to solidify in the mold, wherein the solidified melt is in the form of spherical particles characterized by a specific gravity of about 1.5 to 2.0, a porosity of about 16 to 54%, an average diameter of about 0.1 to 1.7 mm, and a crush strength of at least about 10,000 psi, wherein at least about 80% of the spherical particles are characterized by a diameter within 20% of the average diameter, thereby preparing the proppant material.
2. The method of claim 1 , wherein each of the plurality of oxides is selected from the group consisting of SiO 2 , Al 2 O 3 , Fe 2 O 3 , FeO, Fe 3 O 4 , CaO, MgO, MnO 2 , MnO, Na 2 O, SO 3 , K 2 O, TiO 2 , V 2 O 5 , Cr 2 O 3 , SrO, ZrO 2 , 3Al 2 O 3 2SiO 2 , 2Al 2 O 3 SiO 2 , Ca 2 Mg(Si 2 O 7 ), Ca 2 SiO 4 , and CaCO 3 .
3. The method of claim 1 , wherein the reaction mixture further comprises one or more additives selected from the group consisting of C, Al, Si, Mg, K, Fe, Na, B, O, N, ZrO 2 , Y 2 O 3 , volcanic ash, and aluminum dross.
4. The method of claim 1 , wherein the reactive atmosphere comprises N 2 , O 2 , air, CO 2 , or combinations thereof.
5. The method of claim 1 , wherein the reaction mixture is heated to a temperature of about 800 to 2,500° C.
6. The method of claim 1 , wherein the plurality of oxides are present in the form of waste stream material.
7. The method of claim 1 , wherein the reaction mixture further comprises aluminum dross.
8. The method of claim 1 , wherein the plurality of oxides comprises about 20-99% metallurgical slag and 1-80% flyash, by weight.
9. The method of claim 1 , wherein the spherical particles are characterized by a sphericity of about 0.7 to 1.0.
10. The method of claim 1 , further comprising:
loading a powder comprising the reaction mixture into the mold prior to heating the reaction mixture.
11. The method of claim 1 , wherein at least a portion of the spherical particles comprise a hollow core.
12. The method of claim 1 , further comprising coating the spherical particles with a material comprising an organic material, a ceramic material, or a nitride material.
13. The method of claim 12 , wherein the organic material comprises a phenolic polymer, a polyurethane, or both.
14. A method of preparing a proppant material comprising:
heating a reaction mixture comprising a plurality of oxides from a combination of metallurgical slag and flyash, wherein the reaction mixture is heated in a reactive atmosphere to a temperature above the melting point of the reaction mixture to form a melt; and
allowing the melt to solidify, thereby preparing the proppant material, wherein the proppant material is in the form of spherical particles characterized by a specific gravity of about 1.0 to 2.0, a crush strength of at least about 10,000 psi, a porosity of about 16 to 54%, an average diameter of about 0.1 to 1.7 mm, and a sphericity of about 0.7 to 1.0, wherein at least about 80% of the spherical particles are characterized by a diameter within 20% of the average diameter.
15. The method of claim 14 , wherein each of the plurality of oxides is selected from the group consisting of SiO 2 , Al 2 O 3 , Fe 2 O 3 , FeO, Fe 3 O 4 , CaO, MgO, MnO 2 , MnO, Na 2 O, SO 3 , K 2 O, TiO 2 , V 2 O 5 , Cr 2 O 3 , SrO, ZrO 2 , 3Al 2 O 32 SiO 2 , 2Al 2 O 3 SiO 2 , Ca 2 Mg(Si 2 O 7 ), Ca 2 SiO 4 , and CaCO 3 .
16. The method of claim 14 , wherein the reaction mixture further comprises one or more additives selected from the group consisting of C, Al, Si, Mg, K, Fe, Na, B, O, N, ZrO 2 , Y 2 O 3 , volcanic ash, and aluminum dross.
17. The method of claim 14 , wherein the reactive atmosphere comprises N 2 , O 2 , air, CO 2 , or combinations thereof.
18. The method of claim 14 , wherein at least a portion of the spherical particles comprise a hollow core.
19. The method of claim 14 , further comprising coating the spherical particles with a material comprising an organic material, a ceramic material, or a nitride material.
20. The method of claim 19 , wherein the organic material comprises a phenolic polymer, a polyurethane, or both.