Catalyst for fluidized catalytic cracking and method for fluidized catalytic cracking
The present invention relates to a catalyst for fluidized catalytic cracking of hydrocarbon oil containing a framework-substituted zeolite-1 in which zirconium atoms and/or hafnium atoms form a part of a framework of an ultra-stable Y-type zeolite.
1. A method for cracking a hydrocarbon oil comprising contacting the hydrocarbon oil with a catalyst comprising an ultra-stable Y-type zeolite in a fluidized catalytic cracking unit to produce light olefins and gasoline fuel, wherein the ultra-stable Y-type zeolite is a framework-substituted zeolite in which a part of aluminum atoms constituting a zeolite framework thereof is substituted with 0.1-5 mass % zirconium atoms and 0.1-5 mass % titanium ions calculated on an oxide basis.
2. The method according to claim 1 , comprising contacting a hydrocarbon oil having a boiling point range above about 350° C. to said catalyst at a reaction temperature ranging from about 450° C. to about 700° C., a pressure of about 1 to about 10 bars, for from about 0.1 to about 60 seconds, at a catalyst to oil ratio of from about 2:1 to about 30:1.
3. The method according to claim 1 , wherein the fluidized catalytic cracking unit is a downer reactor.
4. The method according to claim 1 , wherein the fluidized catalytic cracking unit is a riser reactor.
5. The method according to claim 1 , comprising carrying out said cracking under conditions effective to maximize production of gasoline and light olefins.
6. The method according to claim 1 , comprising carrying out said cracking under conditions effective to maximize production of light olefins.
7. The method according to claim 1 , wherein said catalyst comprises a mixture of said framework-substituted ultra-stable Y-type zeolite and one or more additional fluidized cracking catalyst materials.
8. The method according to claim 1 , wherein the framework-substituted ultra-stable Y-type zeolite has a crystal lattice constant of 2.430 to 2.450 nm, a specific surface area of about 600 to about 900 m 2 /g, and a molar ratio of SiO 2 to Al 2 O 3 in the range of about 5:1 to about 100:1.
9. The method of claim 1 , wherein said catalyst comprises from 20% to 50% by mass of zeolite.
10. The method of claim 1 , wherein said catalyst comprises from 15% to 25% by mass of inorganic binder.
11. The method of claim 10 , wherein said inorganic binder is silica sol, water glass, or silicic acid liquid.
12. The method of claim 10 , wherein said inorganic binder is basic aluminum chloride, aluminum biphosphate, or alumina sol.
13. The method of claim 10 , wherein said inorganic binder comprises kaolin, clay, activated alumina, porous silica, a rare earth oxide, or a metal trapping agent.
14. The method of claim 13 , wherein said rare earth oxide has formula
RE 2 O 3
and is present at a range of 0 to 3% by mass.
15. The method of claim 14 , wherein RE is Ce, La, Pr, or Nd.
16. The method of claim 1 , wherein the ultra-stable Y-type zeolite has a molar ratio of SiO 2 to Al 2 O 3 in the range of about 20:1 to 100:1.
17. The method of claim 16 , wherein the ultra-stable Y-type zeolite has a molar ratio of SiO 2 to Al 2 O 3 in the range of about 25:1 to 80:1.