Dip-formed synthetic polyisoprene latex articles with improved intraparticle and interparticle crosslinks
A synthetic polyisoprene latex emulsion has pre-vulcanization composition and post vulcanization composition. The pre-vulcanization composition comprises soluble sulfur with high S 8 ring structure that is catalytically broken by a zinc dithiocarbamate. Surfactants present in the pre-vulcanization composition wets synthetic polyisoprene particles and permeates small sized sulfur and accelerator molecules into the interior of these particles thereby pre-vulcanizing the particles. The degree of pre-vulcanization is verified by isopropanol index test. The latex emulsion has post-vulcanization composition with accelerators that crosslink inter-particle region during post vulcanization cure cycle. The dipped synthetic polyisoprene article is substantially uniformly cured both in the inter-particle and intra-particle regions and reliably exhibits high cross link density, uniform distribution of double bonds in TEM and zinc segregation at the boundaries or original particles by electron microprobe analysis. The films exhibit high tensile strength, tensile modulus, tear strength, burst pressure and burst volume.
1. A synthetic polyisoprene elastomeric glove or condom made of a layer of elastomer comprising:
synthetic polyisoprene particles;
inter-polyisoprene particle crosslinks; and
intra-polyisoprene particle crosslinks,
wherein the glove or condom exhibits a fracture surface with an absence of scanning electron microscope-viewable intra-polyisoprene particle and inter-polyisoprene particle features when ruptured at room temperature.
2. The glove or condom of claim 1 , wherein the glove or condom exhibits a substantially conchoidal fracture when fractured at liquid nitrogen temperature.
3. The condom of claim 2 , wherein the condom is formed of two or more thin layers of said elastomer consistent with dipping on a former without coagulant on the former.
4. The glove or condom of claim 2 , wherein the synthetic polyisoprene particles range in size from about 0.2 to about 2.0 micron.
5. The condom of claim 1 , wherein the condom has a tensile strength of at least 30 MPa.
6. The condom of claim 5 , wherein the condom exhibits a substantially conchoidal fracture when fractured at liquid nitrogen temperature.
7. The condom of claim 1 , wherein the condom is formed of two or more thin layers of said elastomer consistent with dipping on a former without coagulant on the former.
8. The glove or condom of claim 1 , wherein said glove or condom exhibits a substantially conchoidal fracture when fractured at liquid nitrogen temperature.
9. The glove or condom of claim 1 , wherein the synthetic polyisoprene particles range in size from about 0.2 to about 2.0 microns.
10. The glove or condom of claim 9 , wherein the glove or condom exhibits a substantially conchoidal fracture when fractured at liquid nitrogen temperature.
11. A synthetic polyisoprene elastomeric glove or condom made of a layer of elastomer comprising:
synthetic polyisoprene particles;
inter-polyisoprene particle crosslinks; and
intra-polyisoprene particle crosslinks,
wherein the glove or condom exhibits a substantially conchoidal fracture when fractured at liquid nitrogen temperature.
12. The condom of claim 11 , wherein the condom is formed of two or more thin layers of said elastomer consistent with dipping on a former without coagulant on the former.
13. The condom of claim 12 , wherein the synthetic polyisoprene particles range in size from about 0.2 to about 2.0 micron.
14. The condom of claim 11 , wherein the condom has a tensile strength of at least 30 MPa.
15. The condom of claim 14 , wherein the condom has an elongation at break of at least 945%.
16. A synthetic, dip-formed polyisoprene elastomeric condom comprising:
prevulcanized synthetic polyisoprene particles,
said synthetic polyisoprene particles bonded to each other through intra-polyisoprene particle crosslinks and inter-polyisoprene particle crosslinks,
wherein the intra-polyisoprene particle crosslinks and the inter-polyisoprene particle crosslinks are such that the molecular weight is less than about 8400 g/mol between the crosslinks.
17. The condom of claim 16 , wherein the condom exhibits a fracture surface with an absence of scanning electron microscope-viewable intra-polyisoprene particle and inter-polyisoprene particle features when ruptured at room temperature.
18. The condom of claim 17 , wherein the intra-polyisoprene particle crosslinks and the inter-polyisoprene particle crosslinks are such that the molecular weight is less than about 8000 g/mol between the crosslinks.
19. The condom of claim 18 , wherein the condom exhibits a fracture surface with an absence of scanning electron microscope-viewable intra-polyisoprene particle and inter-polyisoprene particle features when ruptured at room temperature.
20. The condom of claim 16 , wherein the intra-polyisoprene particle crosslinks and the inter-polyisoprene particle crosslinks are such that the molecular weight is less than about 7500 g/mol between the crosslinks.
21. A synthetic polyisoprene elastomeric condom made of a layer of elastomer comprising:
synthetic polyisoprene particles;
inter-polyisoprene particle crosslinks and intra-polyisoprene particle crosslinks, wherein osmium tetroxide staining after styrene swelling, polymerization and sectioning shows distinct, adjacent said particles, and substantially uniformly distributed isoprene double bonds indicative of the intra-polyisoprene particle crosslinks and inter-polyisoprene particle crosslinks being substantially uniformly distributed among and between the synthetic polyisoprene particles.
22. The synthetic polyisoprene elastomeric condom of claim 21 , wherein the intra-polyisoprene particle crosslinks and the inter-polyisoprene particle crosslinks are such that the molecular weight is less than about 8400 g/mol between the crosslinks.
23. The synthetic polyisoprene elastomeric condom of claim 21 , wherein the intra-polyisoprene particle crosslinks and the inter-polyisoprene particle crosslinks are such that the molecular weight is less than about 8000 g/mol between the crosslinks.
24. The synthetic polyisoprene elastomeric condom of claim 23 , wherein the condom has a tensile strength of about 25 Mpa or higher.
25. The synthetic polyisoprene elastomeric condom of claim 21 , wherein the intra-polyisoprene particle crosslinks and the inter-polyisoprene particle crosslinks are such that the molecular weight is less than about 7500 g/mol between the crosslinks.
26. The synthetic polyisoprene elastomeric condom of claim 21 , wherein the condom has a tensile strength of about 25 Mpa or higher.