Heat insulator
View Patent ↗One aspect of the heat insulator of the present invention includes a porous sintered body having a porosity of 70 vol % or more and less than 91 vol %, and pores having a pore size of 0.8 μm or more and less than 10 μm occupy 10 vol % or more and 70 vol % or less of the total pore volume, while pores having a pore size of 0.01 μm or more and less than 0.8 μm occupy 5 vol % or more and 30 vol % or less of the total pore volume. The porous sintered body is formed from an MgAl 2 O 4 (spinel) raw material and fibers formed of an inorganic material, the heat conductivity of the heat insulator at 1000° C. or more and 1500° C. or less is 0.40 W/(m·K) or less, and the weight ratio of Si relative to Mg in the porous sintered body is 0.15 or less.
1. A heat insulator comprising a porous sintered body having a porosity of 70 vol % or more and less than 91 vol %,
pores having a pore size of 0.8 μm or more and less than 10 μm occupying 10 vol % or more and 70 vol % or less of the total pore volume, while pores having a pore size of 0.01 μm or more and less than 0.8 μm occupying 5 vol % or more and 30 vol % or less of the total pore volume,
the porous sintered body being formed from an MgAl 2 O 4 and fibers formed of an inorganic material,
the heat conductivity of the heat insulator at 1000° C. or more and 1500° C. or less being 0.40 W/(m·K) or less, and
the weight ratio of Si relative to Mg in the porous sintered body being 0.15 or less.
2. The heat insulator according to claim 1 , wherein the weight ratio of Si relative to Mg in the porous sintered body is 0.0001 or less.
3. The heat insulator according to claim 1 , wherein
the porosity is 85 vol % or more and less than 91 vol %, and
pores having a pore size of 0.8 μm or more and less than 10 μm occupy 10 vol % or more and 40 vol % or less of the total pore volume, while pores having a pore size of 0.01 μm or more and less than 0.8 μm occupy 5 vol % or more and 10 vol % or less of the total pore volume.
4. The heat insulator according to claim 2 , wherein
the porosity is 85 vol % or more and less than 91 vol %, and
pores having a pore size of 0.8 μm or more and less than 10 μm occupy 10 vol % or more and 40 vol % or less of the total pore volume, while pores having a pore size of 0.01 μm or more and less than 0.8 μm occupy 5 vol % or more and 10 vol % or less of the total pore volume.
5. The heat insulator according to claim 1 , wherein
the porosity is 70 vol % or more and less than 85 vol %, and
pores having a pore size of 0.8 μm or more and less than 10 μm occupy 40 vol % or more and 70 vol % or less of the total pore volume, while pores having a pore size of 0.01 μm or more and less than 0.8 μm occupy 10 vol % or more and 30 vol % or less of the total pore volume.
6. The heat insulator according to claim 2 , wherein
the porosity is 70 vol % or more and less than 85 vol %, and
pores having a pore size of 0.8 μm or more and less than 10 μm occupy 40 vol % or more and 70 vol % or less of the total pore volume, while pores having a pore size of 0.01 μm or more and less than 0.8 μm occupy 10 vol % or more and 30 vol % or less of the total pore volume.
7. The heat insulator according to claim 1 , wherein the inorganic material is ceramic fibers.
8. A method for producing a heat insulator comprising a porous sintered body having a porosity of 70 vol % or more and less than 91 vol %,
pores having a pore size of 0.8 μm or more and less than 10 μm occupying 10 vol % or more and 70 vol % or less of the total pore volume, while pores having a pore size of 0.01 μm or more and less than 0.8 μm occupying 5 vol % or more and 30 vol % or less of the total pore volume,
the porous sintered body being formed from an MgAl 2 O 4 and ceramic fibers,
the heat conductivity of the heat insulator at 1000° C. or more and 1500° C. or less being 0.40 W/(m·K) or less, and
the weight ratio of Si relative to Mg in the porous sintered body being 0.15 or less,
the method comprising a step of adding the ceramic fibers having a silica content of 5 wt % or less to an aqueous slurry comprising alumina powder and magnesium oxide powder, and firing the resulting mixture to form the porous sintered body wherein the ceramic fibers are present in an amount of 0.5 wt % or more and less than 60 wt % of the porous sintered body.
9. A heat insulator comprising a porous sintered body having a porosity of 85 vol % or more and less than 91 vol %,
pores having a pore size of 0.8 μm or more and less than 10 μm occupying 10 vol % or more and 40 vol % or less of the total pore volume, while pores having a pore size of 0.01 μm or more and less than 0.8 μm occupying 5 vol % or more and 10 vol % or less of the total pore volume,
the porous sintered body being formed from an MgAl 2 O 4 and ceramic fibers,
the heat conductivity of the heat insulator at 1000° C. or more and 1500° C. or less being 0.40 W/(m·K) or less, and
the bulk specific gravity of the heat insulator being 0.6 or less.
10. The heat insulator according to claim 9 , wherein the heat conductivity at 1000° C. or more and 1500° C. or less is not more than 1.5 times the heat conductivity at 20° C. or more and 1000° C. or less.
11. A heat insulator comprising a porous sintered body having a porosity of 70 vol % or more and less than 85 vol %,
pores having a pore size of 0.8 μm or more and less than 10 μm occupying 40 vol % or more and less than 70 vol % of the total pore volume, while pores having a pore size of 0.01 μm or more and less than 0.8 μm occupying 10 vol % or more and less than 30 vol % of the total pore volume,
the porous sintered body being formed from an MgAl 2 O 4 and ceramic fibers, and
the heat conductivity of the heat insulator at 1000° C. or more and 1500° C. or less being not more than 1.5 times the heat conductivity at 20° C. or more and less than 1000° C.