A process for the manufacture of a modified poly(alkylene carbonate) comprising compounding i) at least one poly(alkylene carbonate) and at least one modifying agent having at least three carboxylic acid groups, or ii) at least one carboxylic acid group and at least one anhydride group, or iii) at least two anhydride groups, at a temperature of 120 to 240° C.
1. A composition comprising a poly(alkylene carbonate) having a Mn of 20,000 g/mol or more which has been modified by compounding the poly(alkylene carbonate) with a modifying agent, wherein the modifying agent has: i) at least three carboxylic acid groups, ii) at least one carboxylic acid group and at least one anhydride group, or iii) at least two anhydride groups; and wherein said composition further comprises a particulate filler selected from the group consisting of carbon black, carbon nanotubes, cellulose, layered or tube like aluminosilicates, layered double hydroxides, metal oxides, boron nitride, mica, polyhedral oligomeric silsesquioxane, silica, calcium carbonate, talc, and graphitic fillers.
2. The composition as claimed in claim 1 , wherein the modifying agent comprises two anhydride units.
3. The composition as claimed in claim 1 , wherein the modifying agent is present in an amount of from 0.05 to 5 wt % relative to the amount of poly(alkylene carbonate) and modifying agent present in total.
4. The composition as claimed in claim 1 , wherein the poly(alkylene carbonate) is formed from the copolymerization of an epoxide and carbon dioxide.
5. The composition as claimed in claim 1 , wherein the filler is present in an amount of from 0.05 to 70 wt % relative to the total amount of filler and modified poly(alkylene carbonate).
6. The composition as claimed in claim 1 , wherein the poly(alkylene carbonate) has an Mw of 5,000 D or more.
7. The composition of claim 1 further comprising a second polymer.
8. The composition as claimed in claim 7 , wherein the second polymer is a fluoroelastomer.
9. The composition as claimed in claim 1 , wherein the modifying agent comprises pyromellitic dianhydride or benzophenone-3,3′,4,4′-tetracarboxylic dianhydride.
10. The composition as claimed in claim 1 , wherein the poly(alkylene carbonate) is formed from the copolymerization of propylene oxide, ethylene oxide, cyclohexene oxide, or mixtures thereof and carbon dioxide.
11. The composition as claimed in claim 1 , wherein the filler comprises a multiwalled nanotube, a graphitic filler, calcium carbonate, a montmorillonite nanoclay, a magnesium oxide, a zinc oxide, a zirconium oxide, or a polyhedral oligomeric silsesquioxane.
12. The composition as claimed in claim 7 , wherein the second polymer is a polyolefin, polylactic acid, starch, or polyhydroxy acid.
13. The composition as claimed in claim 1 further comprising a plasticizer.
14. The composition as claimed in claim 1 further comprising a second poly(alkylene carbonate) that is different than the first poly(alkylene carbonate).
15. The composition as claimed in claim 1 , wherein the filler is a multiwalled nanotube.
16. The composition as claimed in claim 1 , wherein the filler is calcium carbonate.
17. The composition as claimed in claim 1 , wherein the composition is electrically conductive.
18. An article comprising the composition as claimed in claim 1 , wherein the article is a film, molded article, extrusion coated article, foamed article or laminate.