NICKEL-COBALT ALLOY
A Ni—Co alloy includes 30 to 65 wt % Ni, >0 to max. 10 wt % Fe, >12 to <35 wt % Co, 13 to 23 wt % Cr, 1 to 6 wt % Mo, 4 to 6 wt % Nb+Ta, >0 to <3 wt % Al, >0 to <2 wt % Ti, >0 to max. 0.1 wt % C, >0 to max. 0.03 wt % P, >0 to max. 0.01 wt % Mg, >0 to max. 0.02 wt % B, >0 to max. 0.1 wt % Zr, which fulfils the following requirements and criteria: a) 900° C.<γ′ solvus temperature<1030° C. with 3 at %<Al+Ti (at %)<5.6 at % and 11.5 at %<Co<35 at %; b) stable microstructure after 500 h of ageing annealing at 800° C. with a ratio Al/Ti>5 (on the basis of the contents in at %).
1 - 17 . (canceled)
18 : An Ni—Co alloy with 30 to 65 wt % Ni, >0 to max. 10 wt % Fe, >12 to <35 wt % Co, 13 to 23 wt % Cr, 1 to 6 wt % Mo, 4 to 6 wt % Nb+Ta, >0 to <3 wt % Al, >0 to <2 wt % Ti, >0 to max. 0.1 wt % C, >0 to max. 0.03 wt % P, >0 to max. 0.01 wt % Mg, >0 to max. 0.02 wt % B, >0 to max. 0.1 wt % Zr, if necessary containing as residual elements:
max. 0.5 wt % Cu
max. 0.015 wt % S
max. 1.0 wt % Mn
max. 1.0 wt % Si
max. 0.01 wt % Ca
max. 0.03 wt % N
max. 0.02 wt % O,
if necessary also containing:
up to 4 wt % V
up to 4 wt % W, wherein
the alloy satisfies the requirements and criteria listed below:
a) 900° C.≦γ′-solvus temperature≦1030° C. at 3 at %≦Al+Ti (at %)≦5.6 at % as well as 11.5 at %≦Co≦35 at %;
b) stable microstructure after 500 h of aging annealing at 800° C. and an Al/Ti ratio≧5 (on the basis of the contents in at %).
19 . Alloy according to claim 18 , which satisfies the requirement “945° C.≦γ′-solvus temperature≦1000° C.”.
20 . Alloy according to claim 18 , with ΔT (δ−γ′)≧80 K and Al+Ti≦4.7 at % as well as with Co contents ≧11.5 at % and ≦35 at %
21 . Alloy according to claim 18 , which has a temperature interval between δ-solvus and γ′-solvus temperatures equal to or greater than 140 K and a Co content ≧15 at % and ≦35 at %.
22 . Alloy according to claim 18 , with a Ti content of ≦0.8 at %.
23 . Alloy according to claim 18 , with a Ti content of ≦0.65 at %.
24 . Alloy according to claim 18 , with a content of 4.7≦Nb+Ta≦5.7 wt %.
25 . Alloy according to claim 18 , with contents of Ti, Al and Co in accordance with the following limit values:
0.05 at %≦Ti≦0.5 at %,
3.6 at %≦Al≦4.6 at %,
15 at %≦Co≦32 at %.
26 . Alloy according to claim 18 , wherein, if necessary, part of the elements Ni and/or Co may be substituted by the element Fe.
27 . Alloy according to claim 18 , wherein it is usable for the following semifinished forms: strip, sheet, wire, bar.
28 . Use of the alloy according to claim 18 as components of an aircraft turbine, especially rotating turbine disks, as well as components of a stationary turbine.
29 . Use of the alloy according to claim 18 , in engine construction, in furnace construction, in boiler construction, in power-plant construction.
30 . Use of the alloy according to claim 18 , as a structural part in oil and gas extraction engineering.
31 . Use of the alloy according to claim 18 , as a structural part in stationary gas and steam turbines.
32 . Use of the alloy according to claim 18 , as a weld filler material.