Catalyst for solid polymer fuel cell and method for manufacturing the same

1. A catalyst for solid polymer fuel cell having catalyst particles comprising platinum, cobalt and manganese supported on a carbon powder carrier, wherein

a composition ratio (molar ratio) among platinum, cobalt and manganese in the catalyst particles is Pt:Co:Mn=1:0.06 to 0.39:0.04 to 0.33,

a peak intensity ratio of a Co—Mn alloy appearing in the vicinity of 2θ=27° is 0.15 or less with respect to a main peak appearing in the vicinity of 2θ=40° in X-ray diffraction analysis of the catalyst particles, and

a fluorine compound having a C—F bond is supported at least on a surface of the catalyst particles,

wherein a peak ratio of a CoPt 3 alloy and a peak ratio of a MnPt 3 alloy appearing in the vicinity of 2θ=32° are each 0.13 or more with respect to a main peak appearing in the vicinity of 2θ=40° in X-ray diffraction analysis of the catalyst particles.

2. The catalyst for solid polymer fuel cell according to claim 1 , wherein the fluorine compound is supported from 3 to 20% by mass with respect to the entire mass of the catalyst.

3. The catalyst for solid polymer fuel cell according to claim 1 , wherein the fluorine compound is a fluorine resin or a fluorine-based surface active agent.

4. The catalyst for solid polymer fuel cell according to claim 1 , wherein a supporting density of the catalyst particles is from 30 to 70%.

5. The catalyst for solid polymer fuel cell according to claim 2 , wherein the fluorine compound is a fluorine resin or a fluorine-based surface active agent.

6. The catalyst for solid polymer fuel cell according to claim 2 , wherein a supporting density of the catalyst particles is from 30 to 70%.

7. The catalyst for solid polymer fuel cell according to claim 3 , wherein a supporting density of the catalyst particles is from 30 to 70%.

8. A method for manufacturing a catalyst for solid polymer fuel cell, the catalyst defined in claim 1 , comprising the steps of:

supporting cobalt and manganese on a platinum catalyst having platinum particles supported on a carbon powder carrier;

subjecting the platinum catalyst that is formed by the supporting step and supports cobalt and manganese to a heat treatment at from 700 to 1100° C.; and

forming a water-repellent layer including a fluorine compound on the catalyst by bringing the catalyst after the heat treatment step into contact with a solution containing the fluorine compound.

9. The method for manufacturing a catalyst for solid polymer fuel cell according to claim 8 , comprising the step of:

eluting cobalt and manganese on the surface of the catalyst particles by bringing the catalyst after the heat treatment into contact with an oxidizing solution at least one time.

10. The method for manufacturing a catalyst for solid polymer fuel cell according to claim 9 , wherein the oxidizing solution is sulfuric acid, nitric acid, phosphorous acid, potassium permanganate, hydrogen peroxide, hydrochloric acid, chloric acid, hypochlorous acid and chromic acid.

11. The method for manufacturing a catalyst for solid polymer fuel cell according to claim 9 , wherein a contact treatment with the oxidizing solution is conducted at a treatment temperature of from 40 to 90° C. for a contact time of from 1 to 10 hours.

12. A method for manufacturing a catalyst for solid polymer fuel cell, the catalyst defined in claim 2 , comprising the steps of:

supporting cobalt and manganese on a platinum catalyst having platinum particles supported on a carbon powder carrier;

subjecting the platinum catalyst that is formed by the supporting step and supports cobalt and manganese to a heat treatment at from 700 to 1100° C.; and

forming a water-repellent layer including a fluorine compound on the catalyst by bringing the catalyst after the heat treatment step into contact with a solution containing the fluorine compound.

13. A method for manufacturing a catalyst for solid polymer fuel cell, the catalyst defined in claim 3 , comprising the steps of:

supporting cobalt and manganese on a platinum catalyst having platinum particles supported on a carbon powder carrier;

subjecting the platinum catalyst that is formed by the supporting step and supports cobalt and manganese to a heat treatment at from 700 to 1100° C.; and

forming a water-repellent layer including a fluorine compound on the catalyst by bringing the catalyst after the heat treatment step into contact with a solution containing the fluorine compound.

14. A method for manufacturing a catalyst for solid polymer fuel cell, the catalyst defined in claim 1 , comprising the steps of:

supporting cobalt and manganese on a platinum catalyst having platinum particles supported on a carbon powder carrier;

subjecting the platinum catalyst that is formed by the supporting step and supports cobalt and manganese to a heat treatment at from 700 to 1100° C.; and

forming a water-repellent layer including a fluorine compound on the catalyst by bringing the catalyst after the heat treatment step into contact with a solution containing the fluorine compound.

15. A method for manufacturing a catalyst for solid polymer fuel cell, the catalyst defined in claim 4 , comprising the steps of:

supporting cobalt and manganese on a platinum catalyst having platinum particles supported on a carbon powder carrier;

subjecting the platinum catalyst that is formed by the supporting step and supports cobalt and manganese to a heat treatment at from 700 to 1100° C.; and

forming a water-repellent layer including a fluorine compound on the catalyst by bringing the catalyst after the heat treatment step into contact with a solution containing the fluorine compound.

16. The method for manufacturing a catalyst for solid polymer fuel cell according to claim 10 , wherein a contact treatment with the oxidizing solution is conducted at a treatment temperature of from 40 to 90° C. for a contact time of from 1 to 10 hours.