Method for preparing polymer microparticles by spray process
The present invention relates to a method for preparing polymer microparticles by a spray process, wherein a polymer solution obtained by dissolving a polyester-based polymer in ethylene carbonate (hereinafter, referred to as “EC”), which is a solvent, is sprayed at a low temperature hydrocarbon or alcohol solution, thereby preparing frozen EC/polymer microparticles, the frozen EC/polymer microparticles are dissolved in a salt aqueous solution, thereby dissolving and removing EC, and the residual EC in water is removed by washing.
1. A method for preparing biodegradable polymer microparticles, comprising:
dissolving a biodegradable polyester polymer in ethylene carbonate (EC) to obtain a polymer/EC solution;
spraying the polymer/EC solution onto an alcohol selected from the group consisting of methanol or ethanol or an aqueous solution thereof where the alcohol has a temperature between −20° C. and 0° C., thus obtaining frozen polymer/EC microparticles;
dissolving and removing EC from the polymer/EC microparticles by adding the polymer/EC microparticles into a salt aqueous solution; and
filtering and washing the microparticles with water so as to eliminate the remaining EC, thus obtaining biodegradable polymer microparticles.
2. The method of claim 1 , wherein the biodegradable polyester polymer is a polymer selected among Polylactic acid (PLA), Polyglycolic acid (PGA), Poly(D,L-lactic-co-glycolic acid) (PLGA), Polycaprolactone (PCL), poly(valerolactone), poly(hydroxybutyrate) and poly(hydroxy valerate) and has a weight average molecular weight of 10,000 to 250,000.
3. The method of claim 1 , wherein the concentration of biodegradable polyester polymer dissolved in the ethylene carbonate (EC) is 1 to 25% (w/v).
4. The method of claim 1 , wherein the concentration of salt in the salt aqueous solution is 5 to 30% (w/v) and wherein the salt is NaCl or CaCl 2 .