Method for producing an ultra high strength material with high elongation
The invention relates to a method for producing an ultra high strength material with high elongation by work hardening an essentially nickel-free austenitic material and then subjecting the material to heat treatment in the temperature range between 200° C. and <1,100° C. within a period from 10 s to 10 minutes.
1. A method for producing an ultra high strength material with high elongation having the following composition (in % by weight) Mn 4-30%, Cr 10-30%, C<1.0%, N<1.0%, Al<1%, Fe remainder, including unavoidable impurities, and then subjecting the material to heat treatment below the recrystallization temperature in the temperature range between greater than 700° C. and <1,100° C. within a period from 10 s to 10 minutes, followed by subjecting the material to 40 to 95% work hardening by cold rolling.
2. A method for producing an ultra high strength material with high elongation by work hardening an austenitic material consisting of making the following composition (in % by weight) Mn>10-30%, C<1.6%, N<1.0%, Al <7%, Si>0.5-<4%, Fe remainder, including unavoidable impurities, and then subjecting the material to heat treatment below the recrystallization temperature in the temperature range between greater than 700° C. and <1,100° C. within a period from 10 s to 10 minutes.
3. The method according to claim 1 , in which the austenitic material is work hardened, in order to set a yield strength R p0.2 between 1150 and 1300 MPa, a tensile strength R m between 1100 and 1700 MPa and an elongation A 80 between 3 and 60%.
4. The method according to claim 1 , characterized in that the heat treatment is carried out continuously on a running strip.
5. The method according to claim 1 , characterized in that the heat treatment is carried out discontinuously on a component that has been cut or punched out of the strip.
6. The method according to claim 1 , characterized in that components are cut or punched out of the work hardened strip and are hot worked in a subsequent step.
7. The method according to claim 1 , characterized in that components are cut or punched out of the work hardened strip and are cold worked in a subsequent step.
8. The method according to claim 1 , further including the step of using the resulting material as a component in the field of automobile and rail vehicle technology.
9. The method according to claim 8 , further including the step of using the component as a bodywork sheet metal part or sheet metal stiffening element, as a structural part or as a vehicle chassis.