Fibrous substrate containing fibers and nanofibrillar polysaccharide
A single-layer fibrous substrate comprising, by dry weight compared with the weight of the substrate: between 39.9 and 87.9% natural fibers refined to above 50° SR; between 12 and 60% nanofibrillar polysaccharide; and between 0.1 and 4% of at least one retention agent.
1. A fibrous substrate comprising, by dry weight compared to the weight of the substrate,
a) between 39.9 and 87.9% natural fibers refined to between 50 and 95° SR;
b) between 12 and 60% nanofibrillar polysaccharide having a diameter or thickness between 5 and 100 nanometers, and a length less than 1 micrometer;
c) between 0.1 and 4% of at least one retention agent; and
d) less than 10% ash content; wherein
a ratio between a thickness of the substrate, expressed in micrometers, and a weight per unit of surface area of the substrate, expressed in grams per square meter, is less than 1.4 μm/(g/m 2 ).
2. The fibrous substrate according to claim 1 , wherein the fibrous substrate has a weight of at least 10 g/m 2 .
3. The fibrous substrate according to claim 1 , wherein the natural fibers are cellulose fibers and wherein the nanofibrillar polysaccharide is nanofibrillar cellulose.
4. The fibrous substrate according to claim 1 , further comprising at least one additive chosen from the group comprising paper wet strength agents, sizing agents, and inorganic salts.
5. The fibrous substrate according to claim 1 , wherein the substrate is a single-layer fibrous substrate.
6. The fibrous substrate according to claim 1 , wherein the substrate comprises a layer in a multilayer fibrous substrate.
7. The fibrous substrate according to claim 1 , wherein the substrate comprises a fatty-substance barrier.
8. The fibrous substrate according to claim 1 , wherein the substrate comprises a release paper.
9. The fibrous substrate according to claim 1 , wherein the substrate comprises a substrate for metallization.
10. The fibrous substrate according to claim 1 , wherein the substrate comprises a substrate for packaging.
11. The fibrous substrate according to claim 6 , wherein the multilayer fibrous substrate includes at least one mechanical strengthening layer.
12. The fibrous substrate according to claim 10 , wherein the substrate for packaging comprises a substrate for agrifood packaging.
13. The fibrous substrate according to claim 12 , wherein the substrate for agrifood packaging comprises a substrate for pet agrifood packaging.
14. The fibrous substrate according to claim 10 , wherein the substrate for packaging comprises a substrate for fatty substance packaging.
15. The fibrous substrate according to claim 14 , wherein the substrate for fatty substance packaging comprises a substrate for butter packaging.
16. The fibrous substrate according to claim 1 , wherein the substrate comprises less than 5% ash content.
17. The fibrous substrate according to claim 1 , wherein the substrate comprises a substrate having an improved grease-barrier level compared to a substrate without nanofibrillar polysaccharide.
18. The fibrous substrate according to claim 1 , wherein the substrate comprises a substrate having a grease-barrier level of less than a threshold of 5% of stained surface.
19. The fibrous substrate according to claim 1 , wherein the ratio between the thickness of the substrate, expressed in micrometers, and the weight per unit of surface area of the substrate, expressed in grams per square meter, is less than 1.14 μm/(g/m 2 ).