Filtration media
A filtration media with improved filtration, strength, tear resistance and air permeability in the form of a relatively thin and lightweight wet-laid fibrous web that has a wet Mullen ratio of 60% to 80% to ensure that the media is flexible enough to be formed into a fluted structure, and strong enough to retain the fluted structure when wound into a roll and to permit further processing without the media becoming too brittle. The filtration media comprises a blend of cellulose and synthetic fibers having a weight percent of 81 wt % to 87 wt % of a weight of the media and a resin binder having a weight of 13 wt % to 19 wt % (preferably about 16 wt %) of the weight of the media.
1. A filtration media comprising a blend of fibers having a weight percent of 81 wt % to 87 wt % of a weight of the media and a resin binder having a weight percent of 13 wt % to 19 wt % of the weight of the media, the media having a caliper of 6-15 mils (0.15-0.38 mm), a density of 14.1 to 16.03 lbs/ft 3 , and a wet-Mullen ratio of 60% to 80%, the blend of fibers comprising curled softwood pulp in an amount of about 32 wt % to about 66 wt % by weight of the filtration media, wherein the curled softwood pulp is of a type that a 60 pounds per 3,000 square feet (98 g/m 2 ) handsheet made exclusively from the curled softwood pulp has a caliper of 16-26 mils (0.41-0.66 mm) and an air permeability of 100-175 cfm (508-889l/m 2 s).
2. The filtration media of claim 1 , wherein the blend of fibers comprises a cellulose fiber component having a weight of about 82.5 wt % to about 96 wt % of the weight of the blend of fibers and a synthetic fiber component having a weight percent of about 4 wt % to about 17.5 wt % of the weight of the blend of fibers.
3. The filtration media of claim 1 , wherein the caliper of the handsheet is 16-23 mils (0.41-0.58 mm).
4. The filtration media of claim 1 , wherein the media has a wet Mullen ratio of 60-75%.
5. The filtration media of claim 2 , wherein the cellulose fiber component further comprises hardwood pulp having a weight percent of about 13 wt % to about 41 wt % of the media.
6. The filtration media of claim 2 , wherein the synthetic fiber component comprises polyester fibers having a denier of 1 to 3 and a length of ¼ to ½ inch (6.35-12.7 mm).
7. The filtration media of claim 1 , wherein the resin comprises a phenolic resin binder with a crosslinking agent.
8. The filtration media of claim 1 , wherein the media has a tear resistance of at least 50 g (490 mN) per 16 ply in the machine direction and at least 60 g (590 mN) per 16 ply in the cross direction.
9. The filtration media of claim 1 , wherein the caliper of the media is about 10 to 12 mils (0,25-0,30 mm).
10. The filtration media of claim 1 , wherein the basis weight of the media is 35 to 45 pounds/3000 square feet (57-73 g/m 2 ).
11. The filtration media of claim 1 , wherein the media has an air permeability of at least 25 cfm (127 l/m 2 s).
12. The filtration media of claim 1 , wherein the media within a filter element has a pressure drop of less than 350 Pa for dust loading of 30 mg/cm 2 when testing with SAE fine dust at a concentration of 200 mg/m 3 and a face velocity of 5 cm/sec.
13. The filtration media of claim 1 , wherein the media has a removal efficiency of at least 20% when measured in accordance with ASTM-125-89, where dust has been substituted for latex particles.
14. The filtration media of claim 1 , wherein the media comprises pores having a maximum pore size of 43 to 63 microns and an average pore size between 10 and 20 microns.
15. The filtration media of claim 5 , wherein the hardwood pulp is eucalyptus.
16. The filtration media of claim 2 , wherein the blend of fibers further comprises hardwood pulp having a weight percent of about 13 wt % to about 41 wt % of the weight of the media.
17. The filtration media of claim 1 , wherein the filtration media has a pressure drop of less than 1000 Pa for dust loading of 1.5 mg/cm 2 when testing with SAE fine dust at a concentration of 150 mg/m 3 and a face velocity of 20 cm/sec.