Molding process for insulation product
A molding process includes the operation of placing insulation material comprising fibers and binder on the fibers in a mold cavity. The molding process further includes the operation of transferring heat to the insulation material to cause the binder to cure.
1. A molding process comprising
providing an uncured blank including fibers and uncured binder,
molding the uncured blank to establish a shaped product having a molded shape that does not change after removal from a mold cavity formed in a mold, the shaped product including the fibers, a first portion of cured binder, and a remainder of the uncured binder,
wherein the uncured binder comprises:
at least 50% by dry weight of a carbohydrate reactant selected from one or more reducing sugars, one or more carbohydrate reactants that yield one or more reducing sugars in situ under thermal curing conditions and combinations thereof; and
at least 10% by dry weight of a nitrogen-containing reactant selected from ammonia, ammonium salts, inorganic amines, inorganic amine salts, organic amines comprising at least one primary amine group, salts of organic amines comprising at least one primary amine group, and combinations thereof.
2. The molding process of claim 1 , wherein the uncured binder is a substantially formaldehyde-free binder.
3. The molding process of claim 1 , wherein the uncured blank is exposed to a temperature of about 200 degrees Fahrenheit to about 500 degrees Fahrenheit.
4. The molding process of claim 1 , wherein the fibers are glass fibers.
5. The molding process of claim 1 wherein the carbohydrate reactant comprises high-fructose corn syrup.
6. The molding process of claim 1 wherein the nitrogen-containing reactant comprises ammonium sulfate, ammonium phosphate or combinations thereof.
7. A molding process comprising
providing an uncured blank including fibers and uncured binder,
molding the uncured blank to establish a shaped product having a molded shape that does not change after removal from a mold cavity formed in a mold, the shaped product including the fibers, a first portion of cured binder, and a remainder of the uncured binder,
wherein curing of the binder consists essentially of a Maillard reaction.
8. The molding process of claim 7 , wherein the uncured binder is a substantially formaldehyde-free binder.
9. The molding process of claim 7 , wherein the uncured blank is exposed to a temperature of about 200 degrees Fahrenheit to about 500 degrees Fahrenheit.
10. The molding process of claim 7 , wherein the fibers are glass fibers.
11. A molding process comprising
providing an uncured blank including fibers and uncured binder,
molding the uncured blank to establish a shaped product having a molded shape that does not change after removal from a mold cavity formed in a mold, the shaped product including the fibers, a first portion of cured binder, and a remainder of the uncured binder,
wherein the cured binder comprises a substantially water insoluble nitrogen containing polymer.
12. The molding process of claim 11 , wherein the uncured binder is a substantially formaldehyde-free binder.
13. The molding process of claim 11 , wherein the uncured blank is exposed to a temperature of about 200 degrees Fahrenheit to about 500 degrees Fahrenheit.
14. The molding process of claim 11 , wherein the fibers are glass fibers.