Anti-extrusion compositions for sealing and wear components
A method and compositions are described which improve extrusion-and creep-resistance of components for use in a high temperature applications including sealing elements and seal connectors among others. The method includes providing a composition having an aromatic polymer and a crosslinking compound, and subjecting the composition to a heat molding process to form the component and crosslink the aromatic polymer.
1. A composition for formation of an extrusion-resistant sealing member, comprising:
an aromatic polymer; and
a crosslinking compound,
wherein the crosslinking compound has a structure according to formula (II) below:
wherein A is an arene moiety having a molecular weight of less than 10,000 g/mol, R 1 is selected from a group consisting of hydroxide (—OH), amine (—NH2), halide, ether, ester, or amide, and x =2.0 to 6.0.
2. The composition according to claim 1 , wherein the polymer is selected from the group consisting of a polyarylene polymer, a polysulfone, a polyphenylene sulfide, a polyimide, a polyamide, a polyurea, a polyurethane, a polyththalamide, a polyamide-imide, an aramid, a polybenzimidazole, and blends, copolymers and derivatives thereof.
3. The composition according to claim 2 , wherein the aromatic polymer is a polyarylene polymer and/or a polysulfone polymer, and blends, copolymers and derivatives thereof.
4. The composition according to claim 3 , wherein the aromatic polymer is a polyarylene ether polymer including polymer repeating having units of structure according to formula (IV) below:
O—Ar 1 —O—Ar 2 m O—Ar 3 —O—Ar 4 n (IV)
wherein Ar 1 , Ar 2 , Ar 3 and Ar 4 are identical or different aryl radicals, m is 0 to 1, and n is 1-m.
5. The composition according to claim 3 , wherein the aromatic polymer is at least one of polyetheretherketone, polyetherketone, polyetherketoneetherketoneketone, polyetherketoneketone, polysulfone, polyphenylene sulfide, polyethersulfone, polyarylsulfone, and blends, copolymers and derivatives thereof.
6. The composition according to claim 1 , wherein the crosslinking compound is 9,9′-(biphenyl-4,4′-diyl)bis(9H-fluoren-9-ol) and has a general structure according to formula (V):
7. The composition according to claim 1 , further comprising a cross-linking reaction additive capable of reacting with the cross-linking compound to form a reactive intermediate in the form of an oligomer, which reactive intermediate oligomer is capable of cross-linking an organic polymer.
8. The composition according to claim 7 , wherein the cross-linking reaction additive is an organic acid which may be glacial acetic acid, formic acid, and/or benzoic acid.
9. The composition according to claim 7 , wherein the cross-linking reaction additive is an acetate compound that has a structure according to formula (III):
wherein M is a Group I or a Group II metal; and R 2 is an alkyl, aryl, or aralkyl group, wherein the alkyl group is a hydrocarbon group of 1 to about 15 carbon atoms having 0 to about 5 ester or ether groups along or in the chain of the hydrocarbon group, wherein R 2 has 0 to about 5 functional groups.
10. The composition according to claim 1 , wherein the composition is an unfilled composition.
11. A sealing component of a sealing assembly formed by a method comprising the step of crosslinking a composition according to claim 1 .
12. A sealing connector having a seal connector body formed by a method comprising the step of crosslinking a composition according to claim 1 .