Rare earth element oxyflouride powder spray material and sprayed article
A spray material comprising rare earth element oxyfluoride particles having an aspect ratio of up to 2, an average particle size of 10-100 μm, and a bulk density of 0.8-2 g/cm 3 , and containing not more than 0.5 wt % of carbon and 3-15 wt % of oxygen is suitable for air plasma spraying. An article having a sprayed coating of rare earth element oxyfluoride has high resistance against plasma etching and a long lifetime.
1. A method for manufacturing a spray material, comprising:
mixing rare earth element oxide particles and rare earth element fluoride particles to form a slurry, the rare earth element oxide has an average particle size of 0.01 to less than 3 μm, and the rare earth element fluoride has an average particle size of 0.1 to less than 3 μm,
agglomerating the mixture of the rare earth element oxide particles and the rare earth element fluoride particle to form agglomerated particles from the slurry, and
firing the agglomerated particles to form a spray powder material.
2. The method of claim 1 , wherein an amount of the rare earth element oxide is 10 to 70% by weight, and an amount of the rare earth element fluoride is the balance.
3. The method of claim 1 , wherein the particles after the firing have an aspect ratio of up to 2, an average particle size of 10 to 100 μm, and a bulk density of 0.8 to 2 g/cm 3 , and wherein the particles after the firing contain no more than 0.5% by weight of carbon and 3 to 15% by weight of oxygen.
4. The method of claim 1 , wherein a rare earth element of the rare earth element oxide and/or the rare earth element fluoride is selected from the group consisting of Y and Group 3 A elements from La to Lu.
5. The method of claim 4 , wherein the rare earth element is selected from the group consisting of Y, Gd and Er.
6. The method of claim 1 , wherein, in the mixing step, an organic polymer is further mixed as a binder.
7. The method of claim 6 , wherein the organic polymer is selected from the group consisting of carboxymethyl cellulose, polyvinyl alcohol and polyvinyl pyrrolidone.
8. The method of claim 1 , wherein in the agglomerating step, the mixture in the slurry is agglomerated by spray drying.
9. The method of claim 1 , wherein in the firing step, the agglomerated particles are fired at a temperature of 600° C. to 1600° C. in air, vacuum or an inert gas atmosphere.
10. The method of claim 1 , wherein the rare earth element oxide has an average particle size of 0.01 to 1.1 μm, and the rare earth element fluoride has an average particle size of 0.1 to 2.5 μm.
11. The method of claim 1 , wherein an amount of the rare earth element oxide is 10 to 40% by weight, and an amount of the rare earth element fluoride is the balance.
12. The method of claim 1 , wherein the particles after the firing have an aspect ratio of up to 2, an average particle size of 10 to 100 μm, and a bulk density of 0.8 to 2 g/cm 3 , and wherein the particles after the firing contain not more than 0.5% by weight of carbon and 3 to 5% by weight of oxygen.
13. The method of claim 1 , wherein water or hydroxyl content in the spray powder material is up to 10,000 ppm.