Semiconductor device, method of fabricating the same, and apparatus used in fabrication thereof

1. A method of fabricating a semiconductor device, the method comprising:

forming a metal layer on an active layer;

applying a first annealing process to the metal layer and the active layer to form a metal silicide layer; and

concentrating impurity ions in the active layer at an interface between the active layer and the metal silicide layer by creating an electric field across the active layer and the metal silicide layer.

2. The method of claim 1 , wherein the first annealing process and the concentrating impurity ions are performed at the same time such that the electric field is created while the first annealing process is applied.

3. The method of claim 1 , wherein

the concentrating impurity ions includes applying a second annealing process to the active layer and the metal silicide layer after the first annealing process, and

the electric field is created during the second annealing process.

4. The method of claim 1 , wherein

the active layer and the metal layer contact each other to define a Schottky junction therebetween, and

the concentrating impurity ions includes applying a voltage that is equal to or lower than 10 volts to the Schottky junction in order to create the electric field.

5. The method of claim 1 , wherein

the first annealing process includes the concentrating impurity ions by creating the electric field across the active layer and the metal silicide layer or the concentrating impurity ions includes a second annealing process that is performed after the first annealing process and includes the creating the electric field across active layer and the metal silicide layer; and

the first and second annealing processes are performed at a temperature of about 150 degrees Celsius to about 1100 degrees Celsius.

6. The method of claim 1 , further comprising:

implanting impurity ions into the active layer, wherein

the implanting impurity ions into the active layer is performed before the forming the metal layer, while the applying the first annealing process is performed, or after the applying the first annealing process is performed.

7. The method of claim 1 , wherein

the concentrating impurity ions in the active layer includes concentrating the impurity ions at an interface between the active layer and the metal silicide layer using an ion implantation process and a second annealing process that are performed after the applying the first annealing process.

8. The method of claim 1 , further comprising:

forming a polysilicon layer on the active layer before the forming the metal layer; and

implanting impurity ions into the polysilicon layer after the applying the first annealing process, wherein

the semiconductor device is a DRAM device,

the forming the metal layer includes forming the metal layer on the polysilicon layer,

and

the concentrating the impurity ions includes creating the electric field during the implanting the impurity ions into the polysilicon layer or during a second annealing process that is performed after implanting the impurity ions into the polysilicon layer.

9. The method of claim 1 , further comprising:

implanting impurity ions into the active layer before the forming the metal layer,

wherein

the semiconductor device is a logic device including a CMOS circuit, and

the concentrating impurity ions includes creating the electric field during the applying the first annealing process or while a second annealing process is performed after the applying the first annealing process.

10. A method of fabricating a semiconductor device, the method comprising:

forming an active layer on a substrate;

forming a metal layer on the active layer;

forming an upper electrode on a top surface of the substrate including the active layer and the metal layer;

forming a lower electrode on a bottom surface of the substrate, the lower electrode configured to provide an ohmic contact between the lower electrode and the substrate; and

annealing the substrate while an electric field is created between the upper electrode and the lower electrode.

11. The method of claim 10 , further comprising:

forming a polysilicon layer on the active layer before the forming the metal layer; and

applying a first annealing process to the polysilicon layer and the metal layer to form a metal silicide layer before the forming the upper electrode.

12. The method of claim 11 , further comprising:

implanting impurity ions into the polysilicon layer before the forming the metal layer

or after the applying the first annealing process,

wherein the impurity ions are concentrated at an interface between the polysilicon layer and the metal silicide layer during the annealing the substrate while the electric field is created between the upper electrode and the lower electrode.

13. The method of claim 10 , further comprising:

implanting impurity ions into the active layer before the forming the metal layer,

wherein

the annealing the substrate while the electric field is created includes,

forming a metal silicide layer between the active layer and the metal layer, and concentrating the impurity ions in the active layer at an interface between the active layer and the metal silicide layer.

14. The method of claim 13 , wherein

the forming the active layer and the metal layer includes forming a body contact region in the substrate and forming a halo region under the body contact region, and

the forming the lower electrode includes forming a heavily doped region in a lower portion of the substrate.

15. The method of claim 13 , wherein

the substrate is a P-type substrate,

the active layer includes PMOS impurity regions of a PMOS transistor and NMOS impurity regions of an NMOS transistor,

the PMOS impurity regions include an N-type well in the substrate, an N-type heavily doped body contact region in the N-type well, and P-type heavily doped source and drain regions in the N-type well,

the NMOS impurity regions include a P-type heavily doped body contact region in the substrate, an N-type halo region under the P-type heavily doped region in the substrate, and N-type heavily doped source and drain regions in the substrate, and

the lower electrode further includes a P-type heavily doped lower impurity region in a lower portion of the substrate.

16. A method of fabricating a semiconductor device, the method comprising:

forming a conductive layer on an active layer; and

performing an annealing process while applying a voltage across the active layer and concentrating impurity ions at an interface between an impurity region of the active layer and the conductive layer.

17. The method of claim 16 , wherein

the forming the conductive layer on the active layer includes forming a metal layer on the active layer and transforming at least a part of the metal layer to a metal silicide layer on the active layer, and

the performing the annealing process while applying the voltage across the active layer and concentrating the impurity ions includes concentrating the impurity ions at an interface between the impurity region of the active layer and the metal silicide layer.

18. The method of claim 16 , wherein

the forming the conductive layer on the active layer includes forming a metal layer on the active layer, and

the performing the annealing process while applying the voltage across the active layer and concentrating the impurity ions includes transforming at least part of the metal layer to a metal silicide layer during the annealing process.

19. The method of claim 16 ,

the active layer and the conductive layer contact each other to define a Schottky junction therebetween, and

the performing the annealing process while applying the voltage across the active layer and concentrating the impurity ions includes creating an electric field across the Schottky junction based on applying the voltage to the Schottky junction in a range that is equal to or lower than 10 volts.

20. The method of claim 16 , wherein the annealing process is performed at a temperature of about 150 degrees Celsius to about 1100 degrees Celsius.