Substrate for liquid filter

1. A substrate for a liquid filter, comprising a polyolefin microporous membrane,

the polyolefin microporous membrane having a water permeation efficiency of 0.51 to 1.20 ml/min·cm 2 at a pressure differential of 90 kPa,

the polyolefin microporous membrane having a bubble point of 0.45 MPa or more and 0.70 MPa or less,

the polyolefin microporous membrane having a compressibility of less than 15%,

the polyolefin microporous membrane having a thickness of 7 to 16 μm,

the polyolefin being a composition of 60 to 80 mass % of an ultrahigh molecular weight polyethylene having a mass average molecular weight of 900,000 or more and 20 to 40 mass % of a high-density polyethylene having a mass average molecular weight of 200,000 to 800,000, and

a weight per unit area of the polyolefin microporous membrane being from 4.5 to 6.0 g/m 2 .

2. The substrate for a liquid filter according to claim 1 , wherein the polyolefin microporous membrane has a heat shrinkage of 15% or more in the width direction after a heat treatment at 120° C. for 1 hour.

3. The substrate for a liquid filter according to claim 2 , wherein the polyolefin microporous membrane has a pore-blocking temperature of more than 140° C.

4. The substrate for a liquid filter according to claim 3 , wherein the polyolefin microporous membrane has a porosity of 50 to 58%.

5. The substrate for a liquid filter according to claim 2 , wherein the polyolefin microporous membrane has a porosity of 50 to 58%.

6. The substrate for a liquid filter according to claim 1 , wherein the polyolefin microporous membrane has a pore-blocking temperature of more than 140° C.

7. The substrate for a liquid filter according to claim 6 , wherein the polyolefin microporous membrane has a porosity of 50 to 58%.

8. The substrate for a liquid filter according to claim 1 , wherein the polyolefin microporous membrane has a porosity of 50 to 58%.

9. The substrate for a liquid filter according to claim 1 , wherein the substrate is obtained by preparing a solution containing a polyethylene composition and a solvent including a volatile solvent having a boiling point of less than 210° C. at least at atmospheric pressure;

melt-kneading the solution, extruding the obtained melt-kneaded article from a die, and cooling and solidifying the same to give a gel-like molded article;

prior to drawing the gel-like molded article in at least one direction, expressing some of the solvent from the gel-like molded article;

drawing the gel-like molded article in at least one direction;

heat set treating the drawn gel-like molded article at heat set temperature of from 126° C. to 136° C. to form a drawn intermediate molded article; and

extracting and washing the solvent from inside of the drawn intermediate molded article.