Bismuth oxide-based addictive for laser marking
The present invention is directed to a bismuth oxide-based additive for laser marking containing oxygen-deficient bismuth oxide represented by the general formula: Bi 2 O (3-x) (provided that x is 0.01 or more and 0.3 or less and x represents the amount of oxygen deficiency calculated according to the formula: x=3−O 1s /Bi 4f ×2 from the ratio (O 1s /Bi 4f ) of the peak area attributed to the 1s electrons of oxygen bonded to bismuth to the peak area attributed to the 4f electrons of bismuth obtained by X-ray photoelectron spectrometry), which enables marking with excellent blackness and contrast without causing undesirable coloration of a resin composition regardless of the type or shape of a resin to be used.
1. An additive for laser marking, comprising oxygen-deficient bismuth oxide represented by the general formula: Bi 2 O (3-x) (provided that x is 0.01 or more and 0.3 or less), wherein in the general formula, x represents the amount of oxygen deficiency calculated according to the following formula (1) from the ratio (O 1s /Bi 4f ) of the peak area attributed to the 1s electrons of oxygen bonded to bismuth to the peak area attributed to the 4f electrons of bismuth obtained by X-ray photoelectron spectrometry:
x= 3−O 1s /Bi 4f ×2 (1).
2. The additive for laser marking according to claim 1 , wherein x is 0.01 or more and 0.1 or less.
3. The additive for laser marking according to claim 1 , wherein an absorptivity α1 at a wavelength of 1064 nm calculated according to the following formula (2) from a diffuse reflectance in the ultraviolet-visible-near-infrared reflectance spectra is from 20 to 80%:
absorptivity=100−diffuse reflectance (%) (2).
4. The additive for laser marking according to claim 1 , wherein an absorptivity α2 at a wavelength of 532 nm calculated according to the following formula (2) from a diffuse reflectance in the ultraviolet-visible-near-infrared reflectance spectra is from 20 to 80%:
absorptivity=100−diffuse reflectance (%) (2).
5. The additive for laser marking according to claim 1 , wherein the additive is obtained by a method including a step of mixing bismuth oxide or a bismuth compound which is converted to an oxide by application of heat and metallic aluminum at a ratio of the latter to the former of 0.001 to 20% by weight by a dry process or a wet process, and a step of heating the resulting mixture at 60 to 400° C. under reduced pressure lower than the atmospheric pressure by 0.05 MPa or more.
6. The additive for laser marking according to claim 5 , wherein the ratio of metallic aluminum to bismuth oxide or a bismuth compound which is converted to an oxide by application of heat is from 0.1 to 5% by weight.
7. A molded material for laser marking, comprising the additive for laser marking according to claim 1 in an amount of 0.01 to 30% by weight.
8. A coating material for laser marking, comprising the additive for laser marking according to claim 1 in an amount of 0.1 to 90% by weight.
9. A coating layer for laser marking, wherein the coating layer is obtained by coating at least one surface of a base material with the additive for laser marking according to claim 1 .
10. An ink for laser marking, comprising the additive for laser marking according to claim 1 in an amount of 0.1 to 90% by weight.
11. The ink for laser marking according to claim 10 , wherein the ink is obtained by covering a substrate selected from a mica flake, a mica flake covered with a metal oxide, an SiO 2 flake, and a glass filler with the additive for laser marking according to any one of claims 1 to 6 or by mixing the additive with the substrate.
12. The ink for laser marking according to claim 10 , wherein the ink contains at least one material selected from the group consisting of an inorganic or organic pigment, a dye, a resin, an organic solvent, a reactive monomeric compound, and a stabilizer.
13. The ink for laser marking according to claim 10 , wherein the resin is a urethane-based resin or an acrylic resin.
14. An ink film layer for laser marking, wherein the ink film layer is obtained by coating at least one surface of a base material with the ink for laser marking according to claim 10 .
15. The ink film layer for laser marking according to claim 14 , wherein the base material is composed of a plastic film, a paper, a metal foil, or a glass.
16. A printed material for laser marking, wherein the printed material is obtained by performing printing on at least one surface of a base material with the ink for laser marking according to claim 10 .
17. The printed material for laser marking according to claim 16 , wherein the base material is composed of a plastic film, a paper, a metal foil, or a glass.
18. A multi-layered body for laser marking, comprising an ink film layer composed of the ink for laser marking according to claim 10 provided on a base material, and a transparent surface protective layer provided on the ink film layer.
19. The multi-layered body for laser marking according to claim 18 , wherein the base material is composed of a plastic film, a paper, a metal foil, or a glass.
20. A laser marking product, wherein the laser marking product is obtained by performing marking by irradiating the molded material for laser marking according to claim 7 , the coating layer for laser marking according to claim 9 , the ink film layer for laser marking according to claim 14 , the printed material for laser marking according to claim 16 , or the multi-layered body for laser marking according to claim 18 with a laser.
21. The laser marking product according to claim 20 , wherein the laser is a YAG laser with a center wavelength of 1064 nm or a green laser with a center wavelength of 532 nm.